LNP™ ELCRES™ EXL9334
DESCRIPTION
LNP ELCRES EXL9334 is based on Polycarbonate (PC) siloxane copolymer resin. It is a UV stabilized, medium flow opaque material suitable for injection
molding (IM) and sheet extrusion applications. This grade offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems,
extreme low temperature ductility (-40°C) characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard
PC. It is available in a wide range of opaque colors and is targeted for a wide range of applications.
GENERAL INFORMATION
Flame Retardant, High Flow, Non Cl/Br flame retardant, Non halogenated flame retardant, Impact
Features
resistant, Low temperature impact, Weatherable/UV stable
Fillers Unreinforced
Polymer Types Polycarbonate (PC)
Processing Techniques Sheet extrusion, Injection Molding
INDUSTRY SUB INDUSTRY
Automotive Aerospace, Recreational/Specialty Vehicles
Building and Construction Building Component
Consumer Ophthalmics, Home Decoration, Home Appliances
Electrical and Electronics Energy Management, Mobile Phone - Computer - Tablets, Lighting
Industrial Electrical, Material Handling
Mass Transportation Rail
TYPICAL PROPERTY VALUES Revision 20241028
PROPERTIES TYPICAL VALUES UNITS TEST METHODS
(1)
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min 58 MPa ASTM D638
Tensile Stress, brk, Type I, 50 mm/min 59 MPa ASTM D638
Tensile Strain, yld, Type I, 50 mm/min 6 % ASTM D638
Tensile Strain, brk, Type I, 50 mm/min 115 % ASTM D638
Tensile Modulus, 5 mm/min 2100 MPa ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 89 MPa ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span 2050 MPa ASTM D790
Tensile Stress, yield, 50 mm/min 56 MPa ISO 527
Tensile Stress, break, 50 mm/min 57 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 108 % ISO 527
Tensile Modulus, 1 mm/min 2000 MPa ISO 527
Flexural Stress, yield, 2 mm/min 87 MPa ISO 178
Flexural Modulus, 2 mm/min 2100 MPa ISO 178
(1)
IMPACT
Izod Impact, unnotched, 23°C NB J/m ASTM D4812
Izod Impact, unnotched, -30°C NB J/m ASTM D4812
Izod Impact, notched, 23°C 750 J/m ASTM D256
© 2024 Copyright by SABIC. All rights reserved
Izod Impact, notched, -30°C 725 J/m ASTM D256
Izod Impact, notched, -40°C 685 J/m ASTM D256
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 65 kJ/m² ISO 180/1A
Tensile Modulus, 5 mm/min 2100 MPa ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 89 MPa ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span 2050 MPa ASTM D790
Tensile Stress, yield, 50 mm/min 56 MPa ISO 527
Tensile Stress, break, 50 mm/min 57 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 108 % ISO 527
Tensile Modulus, 1 mm/min 2000 MPa ISO 527
Flexural Stress, yield, 2 mm/min 87 MPa ISO 178
Flexural Modulus, 2 mm/min 2100 MPa ISO 178
(1)
IMPACT
Izod Impact, unnotched, 23°C NB J/m ASTM D4812
PROPERTIES TYPICAL VALUES UNITS TEST METHODS
Izod Impact, unnotched, -30°C NB J/m ASTM D4812
Izod Impact, notched, 23°C 750 J/m ASTM D256
Izod Impact, notched, -30°C 725 J/m ASTM D256
Izod Impact, notched, -40°C 685 J/m ASTM D256
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 65 kJ/m² ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 70 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
(1)
THERMAL
HDT, 0.45 MPa, 3.2 mm, unannealed 140 °C ASTM D648
Vicat Softening Temp, Rate B/50 140 °C ASTM D1525
HDT, 1.82 MPa, 3.2mm, unannealed 123 °C ASTM D648
CTE, -40°C to 40°C, flow 6.1E-05 1/°C ASTM E831
CTE, -40°C to 40°C, xflow 6.2E-05 1/°C ASTM E831
CTE, 23°C to 80°C, flow 6.1E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 6.5E-05 1/°C ISO 11359-2
Vicat Softening Temp, Rate B/50 139 °C ISO 306
Vicat Softening Temp, Rate B/120 141 °C ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 118 °C ISO 75/Af
(2)
Relative Temp Index, Elec 125 °C UL 746B
(2)
Relative Temp Index, Mech w/impact 110 °C UL 746B
(2)
Relative Temp Index, Mech w/o impact 120 °C UL 746B
(1)
PHYSICAL
Specific Gravity 1.19 - ASTM D792
(3)
Mold Shrinkage, flow 0.4 – 0.8 % SABIC method
(3)
Mold Shrinkage, xflow 0.4 – 0.8 % SABIC method
Melt Flow Rate, 300°C/1.2 kgf 10 g/10 min ASTM D1238
Density 1.19 g/cm³ ISO 1183
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Water Absorption, (23°C/saturated) 0.4 % ISO 62-1
Melt Volume Rate, MVR at 300°C/1.2 kg 9 cm³/10 min ISO 1133
(1)
ELECTRICAL
Comparative Tracking Index (UL) {PLC} 3 PLC Code UL 746A
High Amp Arc Ignition (HAI), PLC 0 3 mm UL 746A
High Amp Arc Ignition (HAI), PLC 1 0.75 mm UL 746A
Hot-Wire Ignition (HWI), PLC 2 3 mm UL 746A
Hot-Wire Ignition (HWI), PLC 3 0.75 mm UL 746A
Volume Resistivity 1E16 Ω.cm ASTM D257
(2)
FLAME CHARACTERISTICS
UL Yellow Card Link E207780-638263 - -
UL Yellow Card Link 2 E207780-638266 - -
UL Recognized, 94V-0 Flame Class Rating ≥1.5 mm UL 94
UL Recognized, 94-5VA Flame Class Rating ≥3 mm UL 94
Glow Wire Ignitability Temperature, 1.5 mm 825 °C IEC 60695-2-13
©Glow
2024 Wire Flammability
Copyright Index,
by SABIC. All 1.5
rights mm
reserved 960 °C IEC 60695-2-12
(4) (5)
INJECTION MOLDING
Drying Temperature 120 °C
Drying Time 3–4 Hrs
Drying Time (Cumulative) 48 Hrs
ELECTRICAL
Comparative Tracking Index (UL) {PLC} 3 PLC Code UL 746A
High Amp Arc Ignition (HAI), PLC 0 3 mm UL 746A
High Amp Arc Ignition (HAI), PLC 1 0.75 mm UL 746A
Hot-Wire Ignition (HWI), PLC 2 3 mm UL 746A
Hot-Wire Ignition (HWI), PLC 3 0.75 mm UL 746A
Volume Resistivity 1E16 Ω.cm ASTM D257
(2)
FLAME CHARACTERISTICS
UL Yellow Card Link E207780-638263 - -
UL Yellow Card Link 2 E207780-638266 - -
UL Recognized, 94V-0 Flame Class Rating ≥1.5 mm UL 94
UL Recognized, 94-5VA Flame Class Rating ≥3 mm UL 94
PROPERTIES TYPICAL VALUES UNITS TEST METHODS
Glow Wire Ignitability Temperature, 1.5 mm 825 °C IEC 60695-2-13
Glow Wire Flammability Index, 1.5 mm 960 °C IEC 60695-2-12
(4) (5)
INJECTION MOLDING
Drying Temperature 120 °C
Drying Time 3–4 Hrs
Drying Time (Cumulative) 48 Hrs
Maximum Moisture Content 0.02 %
Melt Temperature 295 – 315 °C
Nozzle Temperature 290 – 310 °C
Front - Zone 3 Temperature 295 – 315 °C
Middle - Zone 2 Temperature 280 – 305 °C
Rear - Zone 1 Temperature 270 – 295 °C
Mold Temperature 70 – 95 °C
Back Pressure 0.3 – 0.7 MPa
Screw Speed 40 – 70 rpm
Shot to Cylinder Size 40 – 60 %
Vent Depth 0.025 – 0.076 mm
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
(2) UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
(3) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is
recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
(4) NOTE: Back Pressure, Screw Speed, Shot to Cylinder Size and Vent Depth are only mentioned as general guidelines. These may not apply or need adjustment in specific situations such as low
shot sizes, thin wall molding and gas-assist molding.
(5) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall
molding and gas-assist molding.
DISCLAIMER
Any sale by SABIC, its subsidiaries and affiliates (each a “seller”), is made exclusively under seller’s standard conditions of sale (available upon request) unless agreed
otherwise in writing and signed on behalf of the seller. While the information contained herein is given in good faith, SELLER MAKES NO WARRANTY, EXPRESS OR IMPLIED,
INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE
PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each customer must determine the suitability of seller
materials for the customer’s particular use through appropriate testing and analysis. No statement by seller concerning a possible use of any product, service or design is
intended, or should be construed, to grant any license under any patent or other intellectual property right.
© 2024 Copyright by SABIC. All rights reserved