TECAMID 66 GF30 black - Stock Shapes (rods, plates, tubes)

Chem ical Designation Main features Target Industries

PA 66 (Polyamide 66) very high stiffness mechanical engineering
resistant to many oils, greases and fuels aircraft and aerospace technology
Colour
good wear properties automotive industry
black opaque
very high strength
Density high dimensional stability
1.34 g/cm 3 good heat deflection temperature
good weldable and bondable
Fillers
glass fibres
Data generated directly after machining
(standard climate Germany).

Mechanical properties parameter value unit norm comment

Modulus of elasticity 1mm/min 5500 MPa DIN EN ISO 527-2 1) (1) For tensile test: specimen
(tensile test) type 1b
(2) For flexural test: support
Tensile strength 50mm/min 91 MPa DIN EN ISO 527-2 span 64mm, norm specimen.
Tensile strength at yield 50mm/min 91 MPa DIN EN ISO 527-2 (3) Specimen 10x10x10mm
(4) Specimen 10x10x50mm,
Elongation at yield 50mm/min 8 % DIN EN ISO 527-2 modulus range between 0.5
and 1% compression.
Elongation at break 50mm/min 14 % DIN EN ISO 527-2 (5) For Charpy test: support
Flexural strength 2mm/min, 10 N 135 MPa DIN EN ISO 178 2) span 64mm, norm specimen.
(6) Specimen in 4mm
Modulus of elasticity 2mm/min, 10 N 4700 MPa DIN EN ISO 178 thickness
(flexural test)
Compression strength 1% / 2% / 5% 25/46/104 MPa EN ISO 604 3)
5mm/min, 10 N
Compression modulus 5mm/min, 10 N 4100 MPa EN ISO 604 4)
Impact strength (Charpy) max. 7,5J 97 kJ/m2 DIN EN ISO 179-1eU 5)
Ball indentation hardness 216 MPa ISO 2039-1 6)
T hermal properties parameter value unit norm comment
Glass transition temperature 48 °C DIN EN ISO 11357 1) (1) Found in public sources.
(2) Found in public sources.
Melting temperature 254 °C DIN EN ISO 11357 Individual testing regarding
Service temperature short term 180 °C - 2) application conditions is
mandatory.
Service temperature long term 110 °C
Thermal expansion (CLTE) 23-60°C, long. 5 10-5 K -1 DIN EN ISO 11359-1;2
Thermal expansion (CLTE) 23-100°C, long. 5 10-5 K -1 DIN EN ISO 11359-1;2
Specific heat 1.2 J/(g*K) ISO 22007-4:2008
Thermal conductivity 0.39 W/(K*m) ISO 22007-4:2008
Electrical properties parameter value unit norm comment
Silver electrode, 23°C, 14 DIN IEC 60093 1) (1) Specimen in 20mm
surface resistivity 10 Ω
12% r.h. thickness
14 (2) Due to the black colourant
volume resistivity Silver electrode, 23°C, 10 Ω*cm DIN IEC 60093 2) and moisture uptake of the
12% r.h. material the electrical
Dielectric strength 23°C, 50% r.h. 35 kV/mm ISO 60243-1 3) insulation properties cannot
be 100% guaranteed, despite
Resistance to tracking (CTI) Platin electrode, 23°C, 550 / 475 V DIN EN 60112 single measurements
50% r.h., solvent A suggesting otherwise.
(3) Specimen in 1mm
thickness

Other properties parameter value unit norm comment

Water absorption 24h / 96h (23°C) 0.1 / 0.2 % DIN EN ISO 62 1) (1) Ø ca. 50mm, h=13mm
(2) (+) limited resistance
Resistance to hot water/ bases (+) - 2) (3) Corresponding means no
Resistance to weathering (+) listing at UL (yellow card). The
information might be taken
Flammability (UL94) corresponding to HB DIN IEC 60695-11-10; 3) from resin, stock shape or
estimation. Individual testing
regarding application
conditions is mandatory.

Our information and statements reflect the current state of our knowledge and shall inform about our products and their applications. They do not assure or guarantee chemical
resistance, quality of products and their merchantability in a legally binding way. Our products are not defined for use in medical or dental implants. Existing commercial patents
have to be observed. The corresponding values and information are no minimum or maximum values, but guideline values that can be used primarily for comparison purposes
for material selection. These values are within the normal tolerance range of product properties and do not represent guaranteed property values. Therefore they shall not be
used for specification purposes. Unless otherwise noted, these values were determined by tests at reference dimensions (typically rods with diameter 40-60 mm according to
DIN EN 15860) on extruded and machined specimen. As the properties depend on the dimensions of the semi-finished products and the orientation in the component (esp. in
reinforced grades), the material may not be used without a separate testing under individual circumstances. The customer is solely responsible for the quality and suitability of
products for the application and has to test usage and processing prior to use. Data sheet values are subject to periodic review, the most recent update can be found at
www.ensingerplastics.com. Technical changes reserved.