API 571 Exam (Window Aug.
2021)
(1) If the thermal shock damage may be present, which of the following should be checked
Hot\cold injection points
(2) The best method for finding damage from sigma phase is
Metallographic examination
(3) Phenol (carbolic acid) corrosion is most likely to occur in
High velocity areas
(4) Which of the following would be most resistant to chloride stress crack corrosion
Carbon steel alloys
(4) The form of corrosion most often caused by sulfidation is typically described as
General or uniform corrosion
(5) Differential expansion in bimetallic welds can give rise to:
Thermal fatigue
(6) Which of the following can be used to confirm 885 ºF
Bend testing or impact testing
(7) The overhead stream from a crud atmospheric tower condenser with temperature of
300 f begins to condensate water, its hydrochloric acid (HIC) corrosion, which the following
would the best alloy:-
Titanium
(8) amine cracking is most often associated with
Lean amine
(9) Proactive and retroactive positive material identification (useful PMI) for materials
exposed to
Sulfidation
(10) An inspector observes sharp-edged pitting in piping immediately downstream from
control valve the damage has most likely resulted from which damage mechanism?
Cavitation
(11) Which of the following is most significant contributor to flue gas dew point corrosion?
The material temperatures below depoint
(12) Some reduction in brittle fracture may be achieved by:
PWHT
(13) Which of the following material is least susceptible to Hydrogen stress cracking.
ASTM A-193 B7M
(14) What NDT technique is not used for monitoring cavitation damage.
ECT
(15) Atmospheric corrosion rate is expected to be highest at which temperature.
225F
(16) Deaerators which are not stress relieved likely to suffer from which damage
mechanism
Corrosion fatigue
(17) Refer to table, maximum corrosion will occur in which metal combination.
Aluminum with steel
(18) Which technique requires least surface preparation.Decarburization of steel will cause
removal of carbides. Carbon steel in decarburize will be
ACFM