Mdpe Marlex HHM TR-131

Uploaded by

Lily Li
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

For more information and technical assistance contact:

Saudi Polymers Company


PO Box 11221
Jubail Industrial City
Saudi Arabia 31961
Tel: +(966) 3-356-8222
Email: [email protected]
Visit our site: www.saudipolymers.com
SUPERIOR FLEXIBLE PACKAGING RESINS

Marlex HHM TR-131 Polyethylene


®
MEDIUM DENSITY POLYETHYLENE (MDPE)

This medium density polyethylene is an ethylene-hexene This resin meets these specifications:
copolymer and is tailored for blown film applications that • FDA 21 CFR 177.1520(c) 3.2a, use conditions B through
require: H per Table 2 of 21 CFR 176.170(c)
• Soft feel • ASTM D4976 – PE 225
• Good toughness, impact strength and tear resistance • (EU) No. 10/2011
• Good blending characteristics with HDPE HMW resins
For a safety data sheet (SDS), visit our site at
Typical applications for HHM TR-131 include: www.saudipolymers.com
• T-shirt bags
• Shopping bags
• Trash bags

Nominal Resin Properties(1,2) Value (SI Units) Method


Density 0.938 g/cm3 ASTM D1505
Flow Rate (MI, 190 °C/2.16 kg) 0.20 g/10 min ASTM D1238
Flexural Modulus, Tangent – 16:1 span:depth, 12.7 mm/min 760 MPa ASTM D790
ESCR, Condition B (100 % Igepal), F50 > 1,000 h ASTM D1693
Brittleness Temperature, Type A clamp, Type I specimen < -75 °C ASTM D746
Nominal Blown Film Properties at 0.025 mm(1,3) Value (SI Units) Method
Dart Drop (66 cm) 165 g ASTM D1709
Elmendorf Tear MD 30 g ASTM D1922
Elmendorf Tear TD 350 g ASTM D1922
Tensile Strength at Yield MD, 50.8 mm/min 21 MPa ASTM D882
Tensile Strength at Yield TD, 50.8 mm/min 23 MPa ASTM D882
Tensile Elongation at Break MD, 50.8 mm/min 500 % ASTM D882
Tensile Elongation at Break TD, 50.8 mm/min 660 % ASTM D882
1. The nominal properties reported herein are typical of the products, but do not reflect normal testing variance and therefore should not be used for
specification purposes. Values are rounded.
2. The physical properties were determined on compression moulded specimens that were prepared in accordance with Procedure C of ASTM
D4703, Annex A1.
3. Based on 0.025 mm film produced at 4:1 blow-up ratio.
Revision Date: August, 2022

Before using this product, the user is advised and cautioned to make its own determination and assessment of the
safety and suitability of the product for the specific use in question and is further advised against relying on the
information contained herein as it may relate to any specific use or application. It is the ultimate responsibility of the
user to ensure that the product is suited and the information is applicable to the user’s specific application. Saudi
Polymers Company does not make, and expressly disclaims, all warranties, including warranties of merchantability
or fitness for a particular purpose, regardless of whether oral or written, express or implied, or allegedly arising from
any usage of any trade or from any course of dealing in connection with the use of the information contained herein
or the product itself. The user expressly assumes all risk and liability, whether based in contract, tort or otherwise, in
connection with the use of the information contained herein or the product itself. Further, information contained
herein is given without reference to any intellectual property issues, as well as any international laws which may be
encountered in the use thereof. Such questions should be investigated by the user.

Marlex® is a registered trademark of Chevron Phillips Chemical Company LP. Marlex® products are manufactured
under license from Chevron Phillips Chemical Company LP by Saudi Polymers Company.