LEXAN™ COPOLYMER EXL9330
REGION ASIA
DESCRIPTION
EXL9330 is an opaque (PC)- siloxane copolymer resin that offers extreme low temperature (-60 C) ductility in combination with excellent processability.
This UV stabilized, medium flow resin features UL f1/V-0/5VA rating with non-chlorinated, non-brominated flame retardant agents for wide range of
colors. EXL9330 is an excellent candidate for a broad range of applications such as mobile phones, tablets, industrial housings, electric circuit protection,
personal safety helmets, electric vehicle supply equipment (EVSE) housings and connectors.
TYPICAL PROPERTY VALUES Revision 20230607
PROPERTIES TYPICAL VALUES UNITS TEST METHODS
(1)
MECHANICAL
Tensile Stress, yld, Type I, 50 mm/min 58 MPa ASTM D638
Tensile Stress, brk, Type I, 50 mm/min 61 MPa ASTM D638
Tensile Strain, yld, Type I, 50 mm/min 6 % ASTM D638
Tensile Strain, brk, Type I, 50 mm/min 130 % ASTM D638
Tensile Modulus, 50 mm/min 2100 MPa ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 88 MPa ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span 2060 MPa ASTM D790
Tensile Stress, yield, 50 mm/min 55 MPa ISO 527
Tensile Stress, break, 50 mm/min 60 MPa ISO 527
Tensile Strain, yield, 50 mm/min 6 % ISO 527
Tensile Strain, break, 50 mm/min 125 % ISO 527
Tensile Modulus, 1 mm/min 2100 MPa ISO 527
Flexural Stress, yield, 2 mm/min 85 MPa ISO 178
Flexural Modulus, 2 mm/min 2200 MPa ISO 178
Ball Indentation Hardness, H358/30 90 MPa ISO 2039-1
(1)
IMPACT
Izod Impact, notched, 23°C 801 J/m ASTM D256
Izod Impact, notched, -30°C 678 J/m ASTM D256
Izod Impact, notched, -50°C 587 J/m ASTM D256
Izod Impact, notched, 23°C, 6.4mm 640 J/m ASTM D256
Izod Impact, double-gated, 23°C 1068 J/m SABIC method
Instrumented Dart Impact Total Energy, 23°C 52 J ASTM D3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 70 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 55 kJ/m² ISO 180/1A
Izod Impact, notched 63.5*12.7*3.2, 23°C 80 kJ/m² ISO 180/4A
Izod Impact, notched 63.5*12.7*3.2, -30°C 65 kJ/m² ISO 180/4A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 75 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 60 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
(1)
THERMAL
©Vicat
2023Softening Temp,
Copyright by Rate
SABIC. B/50reserved
All rights 142 °C ASTM D1525
HDT, 0.45 MPa, 3.2 mm, unannealed 134 °C ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed 120 °C ASTM D648
HDT, 1.82 MPa, 6.4 mm, unannealed 124 °C ASTM D648
CTE, -40°C to 40°C, flow 6.66E-05 1/°C ASTM E831
Izod Impact, double-gated, 23°C 1068 J/m SABIC method
Instrumented Dart Impact Total Energy, 23°C 52 J ASTM D3763
Izod Impact, unnotched 80*10*3 +23°C NB kJ/m² ISO 180/1U
Izod Impact, unnotched 80*10*3 -30°C NB kJ/m² ISO 180/1U
Izod Impact, notched 80*10*3 +23°C 70 kJ/m² ISO 180/1A
Izod Impact, notched 80*10*3 -30°C 55 kJ/m² ISO 180/1A
Izod Impact, notched 63.5*12.7*3.2, 23°C 80 kJ/m² ISO 180/4A
Izod Impact, notched 63.5*12.7*3.2, -30°C 65 kJ/m² ISO 180/4A
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 75 kJ/m² ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 60 kJ/m² ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU
PROPERTIES
(1) TYPICAL VALUES UNITS TEST METHODS
THERMAL
Vicat Softening Temp, Rate B/50 142 °C ASTM D1525
HDT, 0.45 MPa, 3.2 mm, unannealed 134 °C ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed 120 °C ASTM D648
HDT, 1.82 MPa, 6.4 mm, unannealed 124 °C ASTM D648
CTE, -40°C to 40°C, flow 6.66E-05 1/°C ASTM E831
CTE, -40°C to 40°C, xflow 6.66E-05 1/°C ASTM E831
CTE, 23°C to 80°C, flow 7.2E-05 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 7.7E-05 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate B/50 140 °C ISO 306
Vicat Softening Temp, Rate B/120 142 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 135 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 124 °C ISO 75/Ae
(2)
Relative Temp Index, Elec 125 °C UL 746B
(2)
Relative Temp Index, Mech w/impact 115 °C UL 746B
(2)
Relative Temp Index, Mech w/o impact 125 °C UL 746B
(1)
PHYSICAL
Specific Gravity 1.18 - ASTM D792
(3)
Mold Shrinkage, flow, 3.2 mm 0.4 – 0.8 % SABIC method
(3)
Mold Shrinkage, xflow, 3.2 mm 0.4 – 0.8 % SABIC method
Melt Flow Rate, 300°C/1.2 kgf 10 g/10 min ASTM D1238
Density 1.19 g/cm³ ISO 1183
Water Absorption, (23°C/saturated) 0.35 % ISO 62-1
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg 9 cm³/10 min ISO 1133
(1)
ELECTRICAL
Dielectric Strength, in oil, 3.2 mm 17 kV/mm ASTM D149
Relative Permittivity, 50/60 Hz 2.95 - ASTM D150
Relative Permittivity, 1 MHz 2.9 - ASTM D150
Dissipation Factor, 50/60 Hz 0.0024 - ASTM D150
Dissipation Factor, 1 MHz 0.0085 - ASTM D150
Volume Resistivity >1.E+15 Ω.cm IEC 60093
Surface Resistivity, ROA >1.E+15 Ω IEC 60093
Dielectric Strength, in oil, 3.2 mm 16 kV/mm IEC 60243-1
Relative Permittivity, 1 MHz 2.7 - IEC 60250
Dissipation Factor, 50/60 Hz 0.001 - IEC 60250
Dissipation Factor, 1 MHz 0.0085 - IEC 60250
Comparative Tracking Index 225 V IEC 60112
Relative Permittivity, 50/60 Hz 2.6 - IEC 60250
Comparative Tracking Index (UL) {PLC} 3 PLC Code UL 746A
Hot-Wire Ignition (HWI), PLC 1 ≥3 mm UL 746A
Hot-Wire Ignition (HWI), PLC 2 ≥1.5 mm UL 746A
Hot-Wire Ignition (HWI), PLC 3 ≥0.6 mm UL 746A
High Amp Arc Ignition (HAI), PLC 0 ≥2.3 mm UL 746A
High Amp Arc Ignition (HAI), PLC 1 ≥0.6 mm UL 746A
(2)
FLAME CHARACTERISTICS
© 2023 Copyright by SABIC. All rights reserved
UL Yellow Card Link E207780-102516601 - -
UL Yellow Card Link 2 E207780-228378 - -
UL Recognized, 94-5VA Flame Class Rating ≥3 mm UL 94
UL Recognized, 94-5VB Flame Class Rating ≥2.5 mm UL 94
UL Recognized, 94V-0 Flame Class Rating ≥1.5 mm UL 94
Surface Resistivity, ROA >1.E+15 Ω IEC 60093
Dielectric Strength, in oil, 3.2 mm 16 kV/mm IEC 60243-1
Relative Permittivity, 1 MHz 2.7 - IEC 60250
Dissipation Factor, 50/60 Hz 0.001 - IEC 60250
Dissipation Factor, 1 MHz 0.0085 - IEC 60250
Comparative Tracking Index 225 V IEC 60112
Relative Permittivity, 50/60 Hz 2.6 - IEC 60250
Comparative Tracking Index (UL) {PLC} 3 PLC Code UL 746A
Hot-Wire Ignition (HWI), PLC 1 ≥3 mm UL 746A
Hot-Wire Ignition (HWI), PLC 2 ≥1.5 mm UL 746A
Hot-Wire Ignition (HWI), PLC 3 ≥0.6 mm UL 746A
High Amp Arc Ignition (HAI), PLC 0 ≥2.3 mm UL 746A
PROPERTIES TYPICAL VALUES UNITS TEST METHODS
High Amp Arc Ignition (HAI), PLC 1 ≥0.6 mm UL 746A
(2)
FLAME CHARACTERISTICS
UL Yellow Card Link E207780-102516601 - -
UL Yellow Card Link 2 E207780-228378 - -
UL Recognized, 94-5VA Flame Class Rating ≥3 mm UL 94
UL Recognized, 94-5VB Flame Class Rating ≥2.5 mm UL 94
UL Recognized, 94V-0 Flame Class Rating ≥1.5 mm UL 94
UL Recognized, 94V-1 Flame Class Rating ≥0.8 mm UL 94
UL Recognized, 94HB Flame Class Rating ≥0.6 mm UL 94
Glow Wire Ignitability Temperature, 3.0 mm 825 °C IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.5 mm 825 °C IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.3 mm 825 °C IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.0 mm 825 °C IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.5 mm 825 °C IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.0 mm 825 °C IEC 60695-2-13
Glow Wire Flammability Index, 3.0 mm 960 °C IEC 60695-2-12
Glow Wire Flammability Index, 2.5 mm 960 °C IEC 60695-2-12
Glow Wire Flammability Index, 2.3 mm 960 °C IEC 60695-2-12
Glow Wire Flammability Index, 2.0 mm 960 °C IEC 60695-2-12
Glow Wire Flammability Index, 1.5 mm 960 °C IEC 60695-2-12
Glow Wire Flammability Index, 1.0 mm 960 °C IEC 60695-2-12
Oxygen Index (LOI) 35 % ISO 4589
UV-light, water exposure/immersion F1 - UL 746C
(4)
INJECTION MOLDING
Drying Temperature 120 °C
Drying Time 3–4 Hrs
Drying Time (Cumulative) 48 Hrs
Maximum Moisture Content 0.02 %
Melt Temperature 255 – 315 °C
Nozzle Temperature 250 – 310 °C
Front - Zone 3 Temperature 255 – 315 °C
Middle - Zone 2 Temperature 245 – 305 °C
Rear - Zone 1 Temperature 235 – 295 °C
Mold Temperature 70 – 95 °C
Back Pressure 0.3 – 0.7 MPa
Screw Speed 40 – 70 rpm
Shot to Cylinder Size 40 – 60 %
Vent Depth 0.025 – 0.076 mm
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
(2) UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
(3) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is
recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.,The information stated on Technical Datasheets should
be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
(4) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall
molding and gas-assist molding.
MORE INFORMATION
© 2023 Copyright by SABIC. All rights reserved
For curve data and CAE cards, please visit and register at https://materialfinder.sabic-specialties.com
DISCLAIMER
Any sale by SABIC, its subsidiaries and affiliates (each a “seller”), is made exclusively under seller’s standard conditions of sale (available upon request) unless agreed
otherwise in writing and signed on behalf of the seller. While the information contained herein is given in good faith, SELLER MAKES NO WARRANTY, EXPRESS OR IMPLIED,
Screw Speed 40 – 70 rpm
Shot to Cylinder Size 40 – 60 %
Vent Depth 0.025 – 0.076 mm
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
(2) UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
(3) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is
recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.,The information stated on Technical Datasheets should
be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
(4) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall
molding and gas-assist molding.
MORE INFORMATION
For curve data and CAE cards, please visit and register at https://materialfinder.sabic-specialties.com
DISCLAIMER
Any sale by SABIC, its subsidiaries and affiliates (each a “seller”), is made exclusively under seller’s standard conditions of sale (available upon request) unless agreed
otherwise in writing and signed on behalf of the seller. While the information contained herein is given in good faith, SELLER MAKES NO WARRANTY, EXPRESS OR IMPLIED,
INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE
PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each customer must determine the suitability of seller
materials for the customer’s particular use through appropriate testing and analysis. No statement by seller concerning a possible use of any product, service or design is
intended, or should be construed, to grant any license under any patent or other intellectual property right.
© 2023 Copyright by SABIC. All rights reserved