Special Steels CB10FF: For Cold Deformation and Bearings

1. The document provides information on standard C10C steel, including comparable standards, chemical composition, and mechanical properties. 2. The chemical composition for C10C steel is 0.08-0.12% carbon, max 0.10% silicon, 0.30-0.50% manganese, max 0.025% phosphorus, and max 0.025% sulfur, 0.020-0.060% aluminum. 3. The mechanical properties provided depend on the heat treatment applied and include minimum yield strengths ranging from 380-520 MPa for rod sizes between 2-40mm.

Uploaded by

Rollpass Design
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
128 views1 page

Special Steels CB10FF: For Cold Deformation and Bearings

1. The document provides information on standard C10C steel, including comparable standards, chemical composition, and mechanical properties. 2. The chemical composition for C10C steel is 0.08-0.12% carbon, max 0.10% silicon, 0.30-0.50% manganese, max 0.025% phosphorus, and max 0.025% sulfur, 0.020-0.060% aluminum. 3. The mechanical properties provided depend on the heat treatment applied and include minimum yield strengths ranging from 380-520 MPa for rod sizes between 2-40mm.

Uploaded by

Rollpass Design
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

SPECIAL

C10C - Nr. 1.0214 STEELS

STANDARD REFERENCE:
EN 10263-2: 2017

RODACCIAI REFERENCES AND COMPARABLE STANDARDS


EUROPE ITALY GERMANY FRANCE UK USA

EN 10263-2: 2001 (UNI 7356 - 74) (DIN 1654-2: 89) (NF A 35-564: 83) - ASTM

Grade N° Werkstoff N°
(C10C) (1.0214) CB 10 FF QSt 36 - 3 1.0214 XC 10 FF - -

CHEMICAL COMPOSITION (CAST ANALYSIS) (%)


C Si/ max Mn P / max S / max Al
0,08÷0,12 0,10 0,30÷0,50 0,025 0,025 0,020÷0,060

MECHANICAL PROPERTIES
Untreadted (+U) Spheroidized (+AC) Cold Drawn + Spheroidized Spheroidized
Cold Drawn
or Untreadted + Peeled or as Treated + Peeled + Skin Passed + Cold Drawn
Size (+U +C)
(+U +PE) (+AC +PE) (+U +C +AC + LC) (+AC +C)
mm
Rm (MPa) max Z (%) min Rm (MPa) max Z (%) min Rm (MPa) max Z (%) min Rm (MPa) max Z (%) min Rm (MPa) max Z (%) min
≥2 ≤5 - - - - - - 410 68 - -
>5 ≤10 430 60 380 70 520 58 400 68 470 63
>10 ≤40 430 60 380 70 510 58 400 68 460 63
>40 ≤100 430 60 380 70 - - - - - -

WORKING TEMPERATURES RECOMMENDED


Operation Hot forgings deformation Soft annealing
°C 850÷1100 650÷700
rev. 10/2018

Mark Rodacciai Download APP

SPECIAL STEELS
CB10FF
FOR COLD DEFORMATION AND BEARINGS