Ref.
No JSPL/ANGUL/TDC-A01831A
TECHNICAL DELIVERY CONDITIONS
Rev. 0
TSD-PLATE DIVISION FOR HOT ROLLED PLATES
ANGUL-ODISHA(INDIA) Date of Issue 06/03/2023
Customer Name : K.G.ISPAT AND POWERS PVT
1 Grade and Specification EN 10025-2 S355 J2 + N / IS 2062 E350 C
2 Process Route As per ANNEXURE A
3 Supply Condition Normalizing Rolling, Fully Killed
4 End Uses Structural
5 Chemical Composition Raw Material Grade.
Ladle Analysis Thickness, t (mm) Internal Grade
Elements
Min Max
As per ANNEXURE A As per ANNEXURE A
%C 0.20
%Mn 1.55
%S 0.025
%P 0.025
%Si 0.03 0.45
%Al 0.020
%Cu 0.55
%Cr 0.29
%Ni 0.42
%Mo 0.11
%(V+Nb+Ti) 0.25
%N 0.012
%CE(IIW) 0.45
CE(IIW)=C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15
6 Mechanical Properties
GL S0
Thickness Range YS (MPa) UTS (MPa) Elongation % Bend Test CVN Impact Test
(mm)
(180°)
Internal Energy Energy
Mandrel Temperature (min. (min.
Min Max Min Min Max Min Min
Diameter C ind.) avg.)
(J) (J)
20 25 345 470 630 5.65 22 2t -20 19 27
Tensile and bend test Orientation of test coupon shall be transverse to the rolling direction and Impact test will be done longitudinal to the rolling
direction.
Thickness : 8 <= t <= 20 mm: -0/+0.8 mm
7 Dimensional Tolerance Length = -0/+ 50mm
t > 20 mm: -0/+ As per IS 1852
Mill Edge
i.Customer shall trim plate edges up to 1.5 X thickness or 40 mm, whichever is maximum, on each edge of the plates.
ii. Width Tolerance for plates with Mill edge condition
Width ( w ) Width Tolerance
8 Edge Condition w <= 2500 mm - 0 / + 60 mm
2500 < w <= 3000 mm - 0 / + 80 mm
3000 < w <= 3500 mm - 0 / + 90 mm
3500 < w <= 4000 mm - 0 / + 110 mm
iii. JSPL will not do grinding near the plate edges (refer point i) for any surface imperfections.
iv. Customer / Customer's Representative will not hold any plate if any defect is observed near the edges (refer point i).
9 Surface Inspection As per IS 2062 Clause 7.2
10 Ultrasonic Inspection As per ANNEXURE A
Tensile and bend : 2 Samples each per heat
11 Test Sample Frequency
Impact: 1 sample per heat (1 sample = 3 specimens)
12 Test Certificate EN 10204 : 3.1
Doc no.: REC-PM-TSD-01-07, Rev. No. 00, Effective Date - 28.10.2020 1
Ref.No JSPL/ANGUL/TDC-A01831A
TECHNICAL DELIVERY CONDITIONS
Rev. 0
TSD-PLATE DIVISION FOR HOT ROLLED PLATES
ANGUL-ODISHA(INDIA) Date of Issue 06/03/2023
Customer Name : K.G.ISPAT AND POWERS PVT
13 Packing condition Loose
14 Jindal Standard Stencil Marking
Stencil Marking Hard Stamping
1. Manufacturer's name
Plate Marking 2. Heat No./ Plate No.
3. Grade
4. Size (TxWxL)
5. UT (As per ANNEXURE A)
15 Third party Inspection TPIA Not applicable
Remarks
1. This is a portal generated TDC. Any modification to the conditions laid out needs to be incorporated in the TDC portal itself, in order to
enable such changes during execution at plant.
Initiator Customer Approved
Prepared By (Seal & Signature)
ANNEXURE A
Thick Width Length Quantity Suppy Condition UT Internal Grade Process Route
(mm) (mm) (m) (MT)
20.0 1700 12.00 38.43 Normalizing Rolling ASTM A-578 L-B JA35XPNR01N1 BF>BOF/EAF>LRF>SLABCASTER>RHF>HOT ROLLING
25.0 3000 6.70 39.45 Normalizing Rolling ASTM A-578 L-B JA35XPNR02N1 BF>BOF/EAF>LRF>SLABCASTER>RHF>HOT ROLLING
25.0 2140 9.60 32.25 Normalizing Rolling ASTM A-578 L-B JA35XPNR02N1 BF>BOF/EAF>LRF>SLABCASTER>RHF>HOT ROLLING
25.0 2500 12.00 23.55 Normalizing Rolling ASTM A-578 L-B JA35XPNR02N1 BF>BOF/EAF>LRF>SLABCASTER>RHF>HOT ROLLING
Doc no.: REC-PM-TSD-01-07, Rev. No. 00, Effective Date - 28.10.2020 2