Fosroc Nitocote HEX constructive solutions
Hygiene coating for internal and external applications to
provide resistance towards the growth of bacteria, fungi,
algae and yeast.
Uses Specification
Provides resistance towards the growth of bacteria, fungi, Hygiene coating shall be Nitocote HEX, based on polyurethane-
yeast and algae. Typical areas of application include: acrylic hybrid polymer dispersion and synergising combination
External coating for structures, in moist and humid of biocides. The coating shall be resistant to the growth of
conditions. bacteria, fungi, algae and yeast. It should be resistant to UV
and suitable for external applications.
Wet areas: Kitchens, bathrooms, shower rooms
Phamaceutical industries Nitocote HEX should be applied to achieve a minimum dry film
thickness of 200 microns.
Restaurants
Hospitals
Properties
Food and beverage processing / storage areas
Specific gravity : 1.3
Dairy industries
Solids content
Sports centers (by wt.) : 53%
Animal husbandry (by vol.) : 43%
Domestic situations (ASTM D1644)
Surface drying time
Cold storage areas
(ASTM D1640) : 35-40mins @20°C
10-15 mins @ 35°C
Advantages
4 - 6 mins @ 45°C
Resistant to the growth of bacteria, fungi, yeast and algae Complete cure : 7 days @ 25°C
Non-toxic - free from traditional copper compounds and Chemical resistance : Fully resistant salt solutions
organo-mercurial actives dilute acids and alkalis
Leach and photo resistant Resistance to
UV stable - will not fade or deteriorate in sunlight 100% humidity : Intact
UV resistance : Excellent
Excellent service life - resistant to chlorides and sulphate
Freeze thaw resistance : Resistant
ions plus a wide range of chemicals
Biological Resistance :
Resistant to defacement Bacteria : Bacillus subtilis
Biocidal as well as biostatic (see table at the end of this Desulfovibrio desulfuricans
document) Enterobacter aerogenes
Escherichia coli
Range of colours
Proteus mirabilis
Fast application - Single component Pseudomonas aeruginosa
Matt finish Pseudomonas fluorescens
Staphylococcus aureus
Resistant to sub-zero and high humidity conditions
Streptoccus faecium
Environment friendly - no VOC’s Yeast Candida albicans
Pityrosporium ovale
Description Rhodotorula spp.
Saccharomyces cerevisiae
Nitocote HEX is a high quality water based, single component,
hygiene coating based on aliphatic polyurethane-acrylic hybrid
polymer dispersion. The coating contains synergising blend
of biocides, which imparts high level of resistance towards the
growth of bacteria, fungi, algae and yeast.
It is UV resistant and is suitable for internal and external areas.
Nitocote HEX
Fosroc Nitocote HEX
Fungi Aspergillus spp. The primer is best applied by using portable spray equipment
Alternaria spp. e.g. knapsack-type. A uniform surface appearance (sheen)
Aureobasidium pullulans should be apparent when the required rate of application is
Cladosporium achieved. If any matt, porous patches remain, then a further
- cladosporides
application of Dekguard Primer DG should be made. Ensure
Cladosporium herbarum
Fusarium spp. Dekguard Primer DG is used within its open time of 48hours
Mucor spp. @ 20°C.
Penicillium funiculosum If in any doubt regarding substrate priming, contact the local
Paecilomyces varioti
Fosroc office.
Phoma violacea
Trichoderma viride Mixing
Trichophyton
- mentagrophytes The contents should be thoroughly stirred to disperse any
Algae Anacystis montana possible settlement.
Chlorococcum tetrasporum
Application
Gleocapsa spp.
Snostoc spp. Hand application
Oscillatoria tenuis
Pleurococcus spp. Achieved by brush or roller.
Scenedesmus vacuolatus
Apply at a rate of 0.2 - 0.25 litres per square meter per coat to
Scytonema hofmanii
achieve a minimum wft of 200 - 250 microns. Apply the second
Stichoccus bacillaris
coat at right angles to the first coat after the first coat has been
Synechocystis minima
Trentepohlia spp. cured and before 24hours.
Spray application
Instructions for use
Faster rates of application are possible using airless spray
Surface preparation equipment. Contact the local Fosroc office prior to application
All surfaces must be clean and free from laitance, dirt, dust, oil for technical advice.
and grease. Incase of porous substrates, spray liberal quantity Repairs
of water on the substrate, prior to commencement of
application. Any damaged areas can be readily overcoated to restore the
membrane continuity. The surface is to be properly prepared
Priming using emery cloth to rub down the surface to provide a key and
is to be made dust free, prior to product application.
Internal application
Cleaning
Priming is not required for internal applications. Saturate the
substrate with copious amount of potable water 15mins prior Nitocote HEX can be removed using only clean water, whilst
to application in order to achieve strong bonding. still damp. If left to dry, then use a scourer.
External applications
Limitations
Prime substrate with Dekguard Primer DG. The depth of primer
penetration and coverage are determined by substrate profile, Application should not commence below 10°C or above 50°C.
porosity and general condition. Do not apply on running or standing water or when there are
chances of rain.
Any areas of glass should be masked. Plants, grass, joint
sealants, asphalt and bitumen-painted areas should be Do not use for immersed conditions
protected during application.
Nitocote HEX - Page 2 of 4
Fosroc Nitocote HEX
Estimating Precautions
Nitocote HEX : 10 litre pails Health and safety
Dekguard Primer DG : 20 litre pails
Nitocote HEX should not come in contact with skin or eyes, nor should
they be swallowed.
Coverage
Some people are sensitive to resins, hardeners and solvents. Wear
Nitocote HEX : 2m²/litre (2coat application )
suitable protective clothing, gloves and eye/face protection. Barrier
Dekguard Primer DG : 4m²/litre
creams such as Kerodex Antisolvent or Rozalex Antipaint provide
Note: The coverage figures coated are theoretical, and based upon additional skin protection.
application to a properly prepared substrate. Since application
conditions vary greatly; due to substrate porosity, quality of Should accidental skin contact occur, remove immediately with a resin
surface preparation, application thickness and wastage removing cream such as Kerocleanse Standard Grade Skin Cleanser
factors, the on-site figures may vary from those shown above. or Rozaklens Industrial Skin Cleanser, followed by washing with soap
and water - do not use solvent.
In case of contact with eyes, rinse immediately with plenty of water and
seek medical advice.
If swallowed seek medical attention immediately - do not induce
vomiting.
For further information, please consult the Material Safety Data Sheet
for Nitocote HEX.
Fire
Nitocote HEX is non flammable.
Storage
Shelf life
Nitocote HEX has a shelf life of 12 months, when stored in warehouse
conditions below 25ºC.
Nitocote HEX - Page 3 of 4
Fosroc Nitocote HEX
Additional information
Hot weather working practices
Whilst the performance properties of Nitocote HEX at elevated
temperatures are assured, application under such conditions
can sometimes be difficult. It is therefore suggested that, for
temperatures above 35ºC, the following guidelines are
adopted as a prudent working regime:
(i) Store unmixed materials in a cool (preferably temperature
controlled) environment, avoiding exposure to direct
sunlight.
(ii) Keep application equipment cool, arranging shade
protection if necessary. It is especially important to keep
cool those surfaces of the equipment which will come
into direct contact with the material itself.
(iii) Try to eliminate application in the middle of the day, when
ambient temperatures will be excessively high.
(iv) Ensure that there are sufficient operatives available to
complete application within the pot life of the material.
(v) Have a ready supply of Fosroc Solvent 102 available for
immediate cleaning of tools after use.
* Denotes the trademark of Fosroc International Limited
†
See separate data sheet
Important note
Fosroc products are guaranteed against defective materials and manufacture and are sold subject to its standard Conditions for
the Supply of Goods and Service. All Fosroc datasheets are updated on a regular basis. It is the user’s responsibility to
obtain the recent version.
Head Office
telephone: (+9714) 2039699 fax: (+9714) 2859649 email: [email protected]
Al Gurg Fosroc LLC
Regional offices
Post Box 657, Dubai Abu Dhabi, Al Gurg Fosroc telephone: 673 1779 fax: 673 1449 email: [email protected]
United Arab Emirates Bahrain, YBA Kanoo telephone: 17738200 fax: 17732828 email: [email protected]
Kuwait, Boodai telephone: 4817618 fax: 4832124 email: [email protected]
www.fosroc.com
Oman, Al Amana telephone: 24815080 fax: 24817554 email: [email protected]
Qatar, Tadmur telephone: 4432365 fax: 4419517 email: [email protected]
UAE/0532/11/C