Stainless Steel - Grade 304

Chemical Formula
Fe, <0.08% C, 17.5-20% Cr, 8-11% Ni, <2% Mn, <1% Si, <0.045% P, <0.03% S
Topics Covered
Background

Key Properties

Composition

Mechanical Properties

Physical Properties

Grade Specification Comparison

Possible Alternative Grades

Corrosion Resistance

Heat Resistance

Heat Treatment

Welding

Machining

Dual Certification

Applications
Background
Grade 304 is the standard "18/8" stainless; it is the most versatile and most widely used
stainless steel, available in a wider range of products, forms and finishes than any other. It has
excellent forming and welding characteristics. The balanced austenitic structure of Grade 304
enables it to be severely deep drawn without intermediate annealing, which has made this
grade dominant in the manufacture of drawn stainless parts such as sinks, hollow-ware and
saucepans. For these applications it is common to use special "304DDQ" (Deep Drawing
Quality) variants. Grade 304 is readily brake or roll formed into a variety of components for
applications in the industrial, architectural, and transportation fields. Grade 304 also has
outstanding welding characteristics. Post-weld annealing is not required when welding thin
sections.

Grade 304L, the low carbon version of 304, does not require post-weld annealing and so is
extensively used in heavy gauge components (over about 6mm). Grade 304H with its higher
carbon content finds application at elevated temperatures. The austenitic structure also gives
these grades excellent toughness, even down to cryogenic temperatures.
Key Properties
These properties are specified for flat rolled product (plate, sheet and coil) in ASTM
A240/A240M. Similar but not necessarily identical properties are specified for other products
such as pipe and bar in their respective specifications.

Composition
Typical compositional ranges for grade 304 stainless steels are given in table 1.

Table 1. Composition ranges for 304 grade stainless steel

C Mn Si P S Cr Mo Ni N
Grade
min. - - - - - 18.0 8.0 -
304 -
max. 0.08 2.0 0.75 0.045 0.030 20.0 10.5 0.10
min. - - - - - 18.0 8.0 -
304L -
max. 0.030 2.0 0.75 0.045 0.030 20.0 12.0 0.10
min. 0.04 - - - 18.0 8.0
304H -0.045 - -
max. 0.10 2.0 0.75 0.030 20.0 10.5

Mechanical Properties
Typical mechanical properties for grade 304 stainless steels are given in table 2.

Table 2. Mechanical properties of 304 grade stainless steel

Hardness
Tensile Strength Yield Strength 0.2% Elongation (% in
Grade (MPa) min Proof (MPa) min 50mm) min Rockwell B Brinell (HB)
(HR B) max max
304 515 205 40 92 201
304L 485 170 40 92 201
304H 515 205 40 92 201
304H also has a requirement for a grain size of ASTM No 7 or coarser.

Physical Properties
Typical physical properties for annealed grade 304 stainless steels are given in table 3.

Table 3. Physical properties of 304 grade stainless steel in the annealed condition

Mean Coefficient of Thermal Expansion Thermal Conductivity Specific

Elastic Electrical
Density (mm/m/°C) (W/m.K) Heat 0-
Modulus Resistivity
Grade (kg/m3) 100°C
(GPa) 0-100°C 0-315°C 0-538°C at 100°C at 500°C (nW.m)
(J/kg.K)
304/L/H 8000 193 17.2 17.8 18.4 16.2 21.5 500 720
Grade Specification Comparison
Approximate grade comparisons for 304 stainless steels are given in table 4.

Table 4. Grade specifications for 304 grade stainless steel

Old British Euronorm

UNS No Swedish SS Japanese JIS
Grade BS En No Name
304 S30400 304S31 58E 1.4301 X5CrNi18-10 2332 SUS 304

304L S30403 304S11 - 1.4306 X2CrNi19-11 2352 SUS 304L

304H S30409 304S51 - 1.4948 X6CrNi18-11 - -

These comparisons are approximate only. The list is intended as a comparison of functionally similar materials
not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be
consulted.

Possible Alternative Grades

Possible alternative grades to grade 304 stainless steels are given in table 5.

Table 5. Possible alternative grades to 304 grade stainless steel

Why it might be chosen instead of 304

Grade
301L A higher work hardening rate grade is required for certain roll formed or stretch formed components.

302HQ Lower work hardening rate is needed for cold forging of screws, bolts and rivets.
Higher machinability needed, and the lower corrosion resistance, formability and weldability are
303
acceptable.
316 Higher resistance to pitting and crevice corrosion is required, in chloride environments

321 Better resistance to temperatures of around 600-900°C is needed…321 has higher hot strength.
A lower cost is required, and the reduced corrosion resistance and resulting discolouration are
3CR12
acceptable.
A lower cost is required, and the reduced corrosion resistance and fabrication characteristics are
430
acceptable.
Corrosion Resistance
Excellent in a wide range of atmospheric environments and many corrosive media. Subject to
pitting and crevice corrosion in warm chloride environments, and to stress corrosion cracking
above about 60°C. Considered resistant to potable water with up to about 200mg/L chlorides at
ambient temperatures, reducing to about 150mg/L at 60°C.

Heat Resistance
Good oxidation resistance in intermittent service to 870°C and in continuous service to 925°C.
Continuous use of 304 in the 425-860°C range is not recommended if subsequent aqueous
corrosion resistance is important. Grade 304L is more resistant to carbide precipitation and can
be heated into the above temperature range.

Grade 304H has higher strength at elevated temperatures so is often used for structural and
pressure-containing applications at temperatures above about 500°C and up to about 800°C.
304H will become sensitised in the temperature range of 425-860°C; this is not a problem for
high temperature applications, but will result in reduced aqueous corrosion resistance.

Heat Treatment
Solution Treatment (Annealing) - Heat to 1010-1120°C and cool rapidly. These grades cannot
be hardened by thermal treatment.

Welding
Excellent weldability by all standard fusion methods, both with and without filler metals. AS
1554.6 pre-qualifies welding of 304 with Grade 308 and 304L with 308L rods or electrodes
(and with their high silicon equivalents). Heavy welded sections in Grade 304 may require
post-weld annealing for maximum corrosion resistance. This is not required for Grade 304L.
Grade 321 may also be used as an alternative to 304 if heavy section welding is required and
post-weld heat treatment is not possible.

Machining
A "Ugima" improved machinability version of grade 304 is available in bar products. "Ugima"
machines significantly better than standard 304 or 304L, giving higher machining rates and
lower tool wear in many operations.

Dual Certification
It is common for 304 and 304L to be stocked in "Dual Certified" form, particularly in plate and
pipe. These items have chemical and mechanical properties complying with both 304 and
304L specifications. Such dual certified product does not meet 304H specifications and may be
unacceptable for high temperature applications.
Applications
Typical applications include:

         Food processing equipment, particularly in beer brewing, milk processing & wine making.

         Kitchen benches, sinks, troughs, equipment and appliances

          Architectural panelling, railings & trim

         Chemical containers, including for transport

         Heat Exchangers

         Woven or welded screens for mining, quarrying & water filtration

         Threaded fasteners

         Springs
 

Source: Atlas Steels Australia