WELD PROCEDURE OUALIFICA TION RECORD WPQR No.

: SD-I

ACCORDING TO: Date:24/12 /2006

Base Metal Welding Process

pipe 1 TO I pipe Process
Specificatioor ASTM A928 ASTM A928 ~ r o c k s Is Type GTAW
Grade: UNS S32760 UNS S32760 Filler Metal
Application. PIPE PIPE
Tltick. (mnt): 12.7 12.7 Process 111
Dim: (Inch) 16" 16" Filler Metal Spec. EN 12072
Heu: No: K73964lZO K73964lZO Filler Meral Class. W 2594 N L
FiUer Metal size (mm) 2.4
Trade name METRODE
Brand name ZERON IOOX
Batch No. W02202 1
Weld metal Class None
Joint Design
Trade rame (flux) None
1,L2'3. Brand name flux) None

?
Batch No. flux) None
<'
Baking Temp. ("C) None
I/ . . , ,
..'] ,I
'x. ;T:>
Baking Time (hr) None
I' !..L<>) (
+ Lm -1- I Holding Temp ("C) None

Gas
Welding Position
Process 11)
Test coupon Position 5G Sltieldinggas or gas miu Argon purity 99.9%
Shielding gas Flow rate 12-14 liI/min
Backing gas or gas mix Argon purity 99.9% Backing For :3 passes
Welders
Backing gas Flow rate 20-24 liumin Oxygen % : 0.5% Max
WELDER Nante: WR No. Process
Preheat & Interpass Temp. Technique
MOHAMED OSMAN RG I GTA W
ALI KHAMIS RG2 GTA W Mitt preheat temp. PC) 25 Orifice Diarneter 10.12 mrn
Grinding &
Mar Ittterpass temp. ("CI 94 Inter pass clearring
Brushing
String or Weave Bead Botlt
Post Weld Heat Treatment
Mar weave width (mm) = 39 Electrode Diu
WeldingBead Sequence Multi passes or single
Heating Rate ("C/min) N.A Multi
pass
6s. . .
Soaking temp. ('C) N.A

<. /'
., Holding time (min) N.A

I
, I,, ,/'
7 ..:.<.,<>:!,;l
'I

.'. .
.
1
> Cooling Rare ("C/mirt) N.A

"
' . ~ . ,.>,,, 4 -.>, /
.. I ,. I,3 :mn < Post Weld Heating
1 LI
:! *n & .+
,.L 1 Tentp. ("C) N.A
Time (mint) N.A
 WELD PROCEDURE OUALIFICA TION RECORD WPQR No.: SD-1

ACCORDING TO: Date:24/12 DO06

API 1104 & KBR GSP-0-GN-KL-MT-SPE-0012-C2

Chemical Analysis
Specimen
No.
C% Mn% Si% P% S% Ni% Cr% Cu% Mo% Al% W% N% PREN

017:W.M. 0.017 0.746 0.309 0.0241 0.0002 8.113 24.91 0.703 3.93 0.039 0.6026 0.2365 41.66

PITTING CORROSION SPSPECIMEN A(WRNO.RG1) SPSPECIMEN B(WRNO.RG2)

MICROSCOPIC INVESTIGATION NO SIGN OP PITS NO SIGN OF PITS
SPECIMEN LOSS (mg) 1.29 1.59
MICRO EX4MINA TION
001 :HAZ (R.SIDE) MICRO 1 SEE PAGE 3 OF 1I
002: WELD MICRO 2 SEE PAGE 4 OF 1 1
003:HAZ(L.SIDE) MICRO 3 SEE PAGE 5 OF 1 l
004:HAZ(R.SIDE) MICRO 4 SEE PAGE 6 OF 11
005:WELD MICRO 5 SEE PAGE 7 OF 1 1
006:HAZ(L.SIDE) MICRO 6 SEE PAGE 8 OF 1 I
007:HAZ(R.SIDE) MICRO 7 SEE PAGE 9 OF I I
008:WELD MICRO 8 SEE PAGE 10 OF 1 l
009:HAZ(L.SIDE) MICRO 9 SEE PAGE I I OF I I

Ferrite % & Sigma Phase %

FERRITE CONTENT IN WELD METAL :54% SIGMA PHASE MAX. 0.28%

FERRITE CONTENT IN HEA T AFFECTED ZONE :50% SIGMA PHASE MAX. 0.21 %

FERRITE CONTENT IN BASE METAL : 47 % :49% N.A

Nitride & Carbide %

THE INTER METALLIC PHASES IN WELD METAL & F EXCEED I %

TEST RESUL TS 4 pt BENDS PITTING CORROSION TEST RESULTS AT 132OC

En Corrosion Corros.
STL END STL Weight Pit Depth
TEMP. Observations ~ ~ ~ Rate~
NO. PH PH No. pH Loss(& (microns)
Ph ) (mndyr)
M192A No Cracking ~ 1 9 2 ~ 0.001 4.001 No Pitting 0
1320c 5'59 4'95 5'
M192B No Cracking ~ 1 9. 2 ~ 4.62 0.001 4.001 No Pitting 0
6
M192F No Cracking ~ 1 9 2 ~ 0.002 4.001 No Pitting 0
90°C 5.36 4'52
M192G No Cracking

Start pH = pH o f solution after saturation with C 0 2

test and N purging
Mpa: Mega Pascal
Lo: Original Gauge Length
R.B. : Root Bend
 Masria for Testing Materials
Tel. IFax: +203 5405072
MTM
Test Certificate

Company : PETROJET- Marine Department Ord. No. : FO36106

Client : GUPCO Date Tested : 111 10 12006
Project : SAQARA PIF PROJECT Date Reported : 12 110 12006

Item : PQR NO. SD-1, P i ~ IeP i ~ e0

( 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

-
Specification :API 1104 & KBR Spec. No. GSP- 0 GN - KL - MT - SPE - 0012 - C2

Tensile Test
Dimensions Area G.L. YS UTS % El Comments
(mm} (mm') {mm) (N l m m ' ) (Nlmm'}
001 : Cross weld 25.1 X 12.5 313,7 NIA NIA 819,3 NIA See Below
002 : Cross weld 24.6 X 12.5 307.5 NIA NIA 832.5 NIA See Below
003 : Cross weld 24 X 12.55 301.2 NIA NIA 830 NIA See Below
004 : Cross weld , 24.7 X 12.55 ,
310 NIA . NIA 829 NIA See Below
- 7
ltem 001: Parent Break Gulf Of Suez Petroleun 1 ' .
Item 002: Parent Break GUPCO
Sitqqarafilaadia Pro.ierf .
ltem 003: Parent Break Dare : 1 1206.4,
ltem 004: Parent Break

Nick Break Test

Dimensions Result Comments
(mm)
005:Cross Weld 19.2 X 12.5 Acceptable Nil
006:Cross Weld 19.1 X 12.4 Acceptable Nil
007:Cross Weld 19.2 X 12.5 Acceptable Nil
008:Cross Weld 19.2 X 12.5 Acceptable Nil

Bend Test
Dimension
(mm) Bend Angle Result Comments
009: Face Bend 10 180" Acceptable Nil
010: Face Bend 10 180" Acceptable Nil
011: Face Bend 10 180" Acceptable Nil
012: Face Bend 10 180" Acceptable Nil
013 : Root Bend 10 180" Acceptable Nil
014 : Root Bend 180" Acceptable Nil
10
015 : Root Bend 180" Acceptable Nil
016 : Root Bend 10 Acceptable Nil
10 180"

Chemical Analysis
C% Mn% Si% P% S% Ni% Cr% Cu% Mo% Al% W% N % PREN
017: Weld Metal 0.017 0.746 9.309 0.0241 0.0002 8.113 24.91 0.703 3.93 0.039 0.6026 0.236-
, - '.)*

i, Alexandria. Egypt
 Masria for Testing Materials
Tel. I Fax: +203 5405072
MTM
Company : PETROJET- Marine Department Ord. No.: F036 106

Item : PQR NO. SD-1, Pipe IPipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

Charpy V Notch Test

Test . Energy Absorbed Average
Dimension Result Comments
Temp. { Joules } {Joules )
018: Weld Metal '
019: Fusion Line 'I0 - 46 '
162
256
106
244
152
261
140
253.7
Acceptable
Acceptable
Nil
Nil

Hardness Survey
Position Method Load Number of Details
Traverses
020: Weld Macro 1 Vickers 10.00 4 294 See Table Page 3 of 4

Macro Examination
Position Result Comments Details
021; weld Macro 1 Acceptable Nil See Page 4 of 4

C~hificateComments: Samples were cut by Petrojet and prepared by MTM

.................................................................................................. END OF TEXT ................................................................................................

Tested by : Masria for Testing Materials

Witnessed by : .........
 Masria for Testlng Materials
Tel. / Fax: +203 5405072
MTM
Company: PETROJET- Marine Department Ord. No.: F036 1 06

Item : PQR NO, SD-1, Pipe I Pipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

Hardness Survey

ltem 20 ( Macro1)

Point
1 256 .
2 266

Page 3 of 4

3 Abo El-Arab Street, Miami, Alexmdria. Egypt Tel.1 Fax: +203 5405072
 Masria for ~ a t i n pMatwiak
Tel. I Fax: +203 5405072
MTM
Company: PETROJET- Marine Department Ord. No.: F036 1 06

Item : PQR NO. SD-1, Pipe I Pioe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

Photographs
Position Magnification
Item 21: Macro Section Macro 1 X 1.5

Page 4 of 4
3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 SHEFFIELD TESTING LA80RATORIES ltd. PAGE 2 OF 10 PAGES

3.0 Teat Specimen Sizes

The four point bend specimens for SSC testing were 130-135mrn long x 15 mm wide x
6.0rnm thick. The bore surface was machined flat and ground to a uniform finish; the
outer surface was machirped to reduce the specimen thickness to 8.0mm

The pitting specimens were 50mm long x 25mm wide and full wall thickness. All pitting
sample bore and outer surfaces were abraded with 12Qgrit paper.
4.0 Test Conditions

The SSC test conditions as defined by the d i n t for tmting were as follows:

The test solution was fully p r o d u d Saqqara water as defined in Table 2 beiow.

Table 2 - Fuly P r o d d Saqqanr Water

The gas environment was 0.4 bara H$5 and 27.6 bara C02 giving a total pressure of
28.0 bara. This gas mix and pressure were produced from a 1.43% H2S in C02 in a
cylinder provided and certified by Scott Specialty gases.

Duplicate tests on Bach weld were carried out at 900C and 132% and test duration was
720 hours

The pitting test conditions as definsd by the dient for testing were as follows:

The test solution was fully produced Saqqara water as M ~ n e d

in Table 2.

The gas environment was 0.08 bara H2S and 4.18 bara CO1 giving a total pressure of
4.24 bara. This gas mix and pressure were produced from a I.43% H2S in COz in a
cylinder provided and certifikd by Scott Specialty Gases.

Triplicate tests on each weld were carried out at 132OC and test duration was 720
hours.
8.0 Specimen Examination

The bend specimens were examined for cracking using a binocular microscope at up to
x40 magnification in the stressed condition (in the stressing jigs) and again in the
unstressed condition (after removal from the stressing jigs).

Any bend specimens that were found not to have cracked were further examined by
taking a cross-section longitudinally through the high stress portion of the beam. This
was mounted in a cold set resin and ground and polished to a I micron finish and
examined for evidence of cracking at up to x i 0 0 magnification.

The pitting specimens were examined using a binocular microscope at up to x40 for
evidence of corrosion, cleaned and reweighed. Pits greater than 0.Imm diameter were
to be recorded.

9.0 Results

No cracking was observed on any of the 4 point bend specimens; details of the results
are reported in Table 3.

Table 4 shows the results from the pitting test; no pitting was observed. Corrosion rates
were measured by weight loss as no pits were observed. The corrosion rates measured
by weight loss assume a uniform corrosion rate aver the entire surface of the test
coupons.

Figures 2 and 3 show examples of the SSC test specimens after testing; Figure 2 in the
stressing jig and Figure 3 after removal. Figure8 4 and 5 show the out surface of the
pitting sampks of the main and repair weld respectively before testing, Figures 6 and 7
show these after testing

10.0 Conclusions
Two samples of welded 12mm 25% Cr duplex stainless steel pipe were supplied
representing main and repair weld procedures. Four (4) four point bend specimens and
three (3) pitting specimens were machined from each sample.

The bent beam specimens were tested at 90% and 132% in fully produced Saqqara
water at a total pressure of 28 bar absolute comprising 0.4 bara HzS and 27.6 bara
C02.
The pitting samples were tested at 132OC in fdly produced Saqqara water at a total
pressure of 4.24 bar absolute amprising 0.06 bara H2S and 4.18 bara COz

No evidence of cracking was observed on any four point bend specimens after testing.

No evidence of pitting was observed on any of the outer or bore surfaces of the pitting
specimens after testing.
1 SHEFFlELD TESTING LABORATORIES Ltd. PAGE 6 OF 10 PAGES 1

-
Figure 2 Specimen Ml93F in Jig a b r Testing at 9a°C
 PAGE 9 OF 10 PAGES

Figure 6 - SD-I Pitttng Specimens afker Test

 Masria for ~ n t i n emat^^^
Tel. I Fax: +203 5405072
MT.M
Test Certificate

Company : PETROJET- Marine Department Ord. No. : F047106

Client : GUPCO Date Tested : 11 11212006
Project : SAQARA PIF PROJECT Date Reported : 12 11212006

Item : PQR NO. SD-1, Pipe I Pipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760
- - - -
Specification :API 1104 & KBR Spec. No. GSP- 0 GN KL - MT SPE 0012 C2 -
Micro Examination Location

..-

Page 1 of 15

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tell Fax: +203 5405072
 Masria r~ ~ r t i n ~e aw
T81. I Fax: +203 5405072
b
MTM
Company: PETROJET- Marine Department Ord. No.: F047106

Item : PQR NO. SD-1, Pipe IPipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

I Photographs
I I ~ositin I Magnification I
I OOA: PARENT METAL
I

Micro A
I

X 500

Page 3 of 15

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Masria for ~mtingMaterials
lei. / Fax: +203 5405072 MTM
Company: PETROJET- Marine Department Ord. No.: F047106

Item : PQR NO. SD.1, Pioe IPipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760
I Photographs 1
I Position I Magnification
I
I I

) OOC: PARENT METAL I Micro C X500

Page 5 of 15
>

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Masria tor T=u"~ ~ . t . r i . ~ ~
Tel. i Fax: +203 54QSO72 --
MTM
-

Company: PETROJET. Marine Department Ord. No.: F047106

Item : PQR NO. SD-1, Pipe IPipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

Photographs
Position Magnification
001: HAZ (R. side) Micro 1 X 500

Page 7 of 15

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Masrla tor i - t i g
Tel. I Fax: +203 5405072
~atrci.~~
MTM
Company: PETROJET. Marine Department Ord, No,: F047106

Item : PQR NO. SD-1, Pipe 1 Pipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

Position Magnification
003: HAZ ( L . side ) Mim3 X500

Page 9 of 15

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Masria tor ~ t i n Materials
g
Tel. I Fax: +203 5405072
MTM
Company: PETROJET- Marine Department Ord. No.: F047106

Item : PQR NO. SD-1, Pipe IPipe( 0 16 " X 12.7 MU) material ASTM, A928 UNS S 32760

Position Magnification
005: WELD Micro 5 X500

Page 11 of 15

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Masrla for Testing M ~ M ~ I S
Tel. I Fax: +203 W 5 0 7 2
MTM
Company: PETROJET- Marine Department Ord. No.: F047106

Item : PQR NO. SD-1, Pipe I Pipe( O 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

Photographs
Position Magnification
007: HAZ ( R . side ) Micro 7 X 500

Page 13 of 15
-

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Masfla tor Testing mmrll~~
Tel. / Fax: +203 5405072
MTM
Company: PETROJET- Marine Department Ord. No.: F047106

:I ltm : PQR NO. SD-1. Pipe IPipe( 0 16 " X 12.7 MM) material ASTM. A928 UNS S 32760

I 1 Position I Magnification

Page 15 of 15

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 PENETRANT TESTING REPORT
"3 UKAS
. IS,.+,\ ~ " n
General Marine Dept. 00 1

Q C - 17
 -
Masria for Testing Materials
Tel. / Fax: +203 5405072
MTM
Test Certificate

Company : PETROJET- Marine Department Ord. No. : F036106

Client : GUPCO Date Tested : 11110 12006
Project : SAQARA PIF PROJECT Date Reported : 12 110 12006

Item : PQR NO. SD-1, Pipe IPipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760
- - - -
Specification :API 1104 8 KBR Spec. No. GSP- 0 GN KL MT SPE 0012 C2- -

Micro Examination Location

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Masria for Testing Materials
Tel. / Fax: +203 5405072
MTM
Company: PETROJET- Marine Department Ord. No.: F036106

Item : PQR NO. SD-1, Pipe I Pipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

Photographs
Position Magnification
001: HAZ (R. side) Micro 1 X 500

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Masria for Testing Materials
Tel. / Fax: +203 5405072
MTM
Company: PETROJET- Marine Department Ord. No.: F036106

Item : PQR NO. SD-1. Pipe I Pipe( 0 16 " X 12.7 MM) material ASTM. A928 UNS S 32760

Photographs
Position Magnification
003:HAZ ( L . side ) Micro 3 X 500

Page 5 of 11
3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Masria for Testing Materials
Tel. I Fax: +203 5405072
MTM
Company: PETROJET- Marine Department Ord. No.: F036106

Item : PQR NO. $0-1, P i ~ IePiw( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

I Photographs 1
Position Magnification
005:WELD Micro 5 X 500

Page 7 of 11
3 Abo El-Arab Street, Miami, Alexandria. Egypt Tell Fax: +203 5405072
 Masria for ~estingMaterials
Tel. I Fax: +203 5405072
MTM
Company: PETROJET- Marine Department Ord. No.: F036106

Item : PQR NO. SD-1, Pipe I Pipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

Photographs
Position Magnification
007:HAZ (R. side) Micro 7 X 500

Page 9 of 11
3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Masria f~ Testing Materials

Tel. / Fax: +203 5405072

MTM
Company: PETROJET- Marine Department Ord. No.: F036106

Item : PQR NO. SD-1, Pipe IPipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

I Photographs
Position Magnification
009: HAZ ( L .side ) Micro 9 X 500

Page 11 of 11
3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1Fax: +203 5405072
 Masria for Testing Materials
Tel. / Fax: +203 5405072
MTM
Test Certificate

Company : PETROJET- Marine Department Ord. No. : F036106

Client : GUPCO DateTested :l111012006
Project : SAQARA PIF PROJECT Date Reported : 12 1 10 1 2006

Item : PQR NO. SD-1, Pipe IPipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

Specification :API 1104 , KBR Spec. No. GSP- 0 - GN - KL MT SPE 0012 C2 & ASTM 648 - - - -
PllllNG CORROSION TEST
Test Method : A ferric chloride pitting test according to ASTM G 48 Method A.

Specimens : Specimen A ( WR No. RGI ) & Specimen B ( WR No. RG2 )

: Specimens surfaces were polished to uniform finish by wet polishing with A-120 grit abrasive
?? Surface Preparation paper followed by 24 hrs dr passivation
Time of test : 24 hours in ferric chloride solution

Test temperature : 35°C +1 "C

RESULTS

Certitkate Comments: Samples wen cut by Petrojet and prepared by MTM

...........................................................................................................OF TEXT................................................................................................

Tested by :Masria for Testing Materials

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Masria for Testing Materials
Tel. I Fax: +203 5405072
MTM
Company: PETROJET- Marine Department Ord. No.: F036106

Item : PQR NO. SO-1, Pipe I Pipe( 0 16 " X 12.7 MMI material ASTM, A928 UNS S 32760

Photographs -
Position
Specimen B (WR No. RGZ ) Test face

Paae
-- 3 of 3

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tell Fax: +203 5405072
 Masria for Testing Materials
Tel. / Fax: +203 5405072
MTM
Company: PETROJET- Marine Department Ord. No.: F036106

Item : PQR NO. SD-1, Pipe I Pipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

- - - - -
Specification :API 1104, KBR Spec. No. GSP- 0 GN KL MT SPE - 0012 C2 & ASTM G48

Photographs
Position
Specimen A (WR No. RG1) Test face

Page 2 of 3

3 Abo El-Arab Street, Miami, Alexandria. Egypt Te1.l Fax: +203 5405072
O9LZE S SNn 8Z6V 'WISV le!Jaleu (WW L'ZC X ,, 9C 0 Pd!d Iad!d 'C-aS 'ON tlbd : wall
90 19EOd :'ON 'PJO lualuuedaa auueyy -13roa13d :Aueduo3
O9LZE S SNn 8Z6V 'WISV le!J@WM(WW L'ZC X ,,9C 0 Pd!d I ed!d 'C-(IS 'ON tlbd : WJI
90 BtOd :'ON 'PJO
 Masria for Testing Materials
Tel. / Fax: +203 5405072
MTM
Company: PETROJET- Marine Department Ord. No.: F036106

Item : PQR NO. SD-1, Pipe 1 Pipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

Photographs
Position Magnification
004: HAZ (R. side) Micro 4 X 500

Page6of 11
3 Abo El-Arab Street, Miami, ~lexandriaEgypt Tell Fax: +203 5405072
 Masria for Testing Materials
Tel. / Fax: +203 5405072
MTM
Company:PETROJET- Marine Department Ord. No.: F036106

Item : PQR NO. SD-1, Pipe I Pipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

Photographs
Position Magnification
002:WELD Micro 2 X 500

Page 4 of 11

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tell Fax: +203 5405072
 Masria for Testing Matelals
Tel. I Fax: +203 5405072
MTM
Company: PETROJET- Marine Department Ord. No.: F036106

Item : PQR NO. SD-1, Pipe I Pipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

The Ferrite Content in Weld Metal 54% volume fraction & Sigma phase max. 0.28%

The Ferrite Content in Heat Affected Zone 50% volume fraction & Sigma phase max. 0.21%

Certificate Comments: Samples were cut by Petrojet and prepared by MTM

........................................................................................................END .............................................

Tested by : Masria for Testing Materials

Witnessed by : .............................................................

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Radiogra~hicT e s t h Report
... .. .

Report No.: 1
SAQQARA P/F (16"GAS LIFT RAISER)
Item: PIPE 16" * 12.7 Drawing 1 QC No.: PQR SD- 1

LOF.: Lack of Fusion FD.: Film Defect

SC. : Suspected Crack R/C. : Root concave UC. : Undercut RJS.: Re Shoot
CIQ.: cut out

QP20n041F06 - Rev. 0
09LZ6 S SNn 8Z6V 'WlSV le!JaWJ(WW L'ZC X ,,9C 0 ) a ! d I a ! d 'C-(IS 'ON tl0d : wl
90 lLPOj :'ON 'PJO
 Masria tor ~ r t i t MatMaIs
~g
Te1.i Fax: +203 t1406072 MTM
Company: PETROJET- Marine Department Ord. No.: F047106

Item : PQR NO. SD-1, Pipe 1 Pipel 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

I Position I
I
Magnification
- I
I
I

mS:HAZ(L.skk) I Micro 6 1 X500

Page 12 of 15
-

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel./ Fax: +203 5405072
 ZLOSOPS €OZ+ :md /'1=l. 1-3 'QIJP-xaIV 'F!N o9v €
' m s qartrartrla
O9LZE S SNn 8Z6V 'WlSV le!Jaleu (NMI L'ZC X .9C 0 )ad!d Ia ! d 'C-US 'ON YBd : wl
 Masria tor T W " ~Materiala
Tel. I Fa: +203 W5072
MTM
Company: PETROJET- Marine Department Ord. No.: F047106

Item : PQR NO. SD-1, Pipe IPipel 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

Page 8 of 15
>

3 Abo El-Arab Street, Miami, Alexandria. Egypt Te1.l Fax: +203 5405072
09LZ& S SNn 8Z6V 'HlSV IelJaleU(WW L'ZC X ,,9C 0W!d Iea!d 'C-(IS'ON tlbd : WJl
90 ILPOA :'ON 'PJO :AUB~UIO~
luaupedaa auueyy -1gr0~13d
 Masria f~ Testing ~ a b r i . b
Tel. I Fax: +203 !MOW72
MTM
Company: PETROJET- Marine Department Ord. No.: F047106

Item : PQR NO. SD-1,Pipe I Pipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

phofographs
Position Magnification
00B: PARENT METAL Micro B X500

Page 4 of 15

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 Masria tar T
Tel. I Fax: +203 5405072
~~ a
B ~ a e
MTM
Company: PETROJET- Marine Department Ord. No.: F047106

Item : PQR NO. SD-1, Pipe 1Pipe( 0 16 " X 12.7 MM) material ASTM, A928 UNS S 32760

The Ferrite Content in Base metal :47 % :49%

The intermetallic phases in weld metal &( HAZ ) nitrides ,carbides not exceed 1%

Certificate Comments: Samples were cut by Petrojet and prepated by MTM

.................................................................................................... E D OF TEXT..................
.........................................................................

Tmted by :Masria for Testing Materials

Witnessed by : ...........

3 Abo El-Arab Street, Miami, Alexandria. Egypt Tel.1 Fax: +203 5405072
 SERIAL No, 6120190
SHEFFIEU) TESTING LABORATORIES L a .

-
Table 3 Test Results 4pt Bends

Ndes: (1) Start pH = pH of solution after saturation with COz

(2) End pH = pH of solution after completion of test and N purging

-
Table 4 Plttlng Cornion Test Resub at 132%
 SHEFFIELD TESTING LABORATORIES Ltd. PAGE 3 O f 10 PAGES

5.0 Four Point &end Specimens

These specimens were rectangular beams 130-135rnm x 15mm x 6.0mm finished to

600 grit. All specimens were marked with an STL test number, cleaned and degreased
with acetone prior to testing.

The specimens were all strain gauged in accordance with EFC 17 and mounted in a 4-
point bend jig.Figure 1 shows an example ofa strain gauged 4-point bend specimen in
a stressing jig. Both iongitudinal and transverse strains were monitored in order to
establish the applied drain. The specimens were deflected in the jigs, until the total
applifed strain was 5 0 0 0 ~this
~ ; equates to 100%of the actual yield stress (AYS).

The gauges were left in position and the strain monitored far up to one hour to detect
any relaxation. If relaxation occurred the specimens were further stressed to obtain the
desired value. No relaxation was detected in any of the stressed b a r n specimens. The
gauges were then removed and the specimens cleaned and disgreased with acetone
prior to testing.

6.0 Pifflng Specimens

These specimens were rectangular coupons 50mm x 25mm x full wall thickness ; the
oxide byer on the bore and outer surfaces was removed by abrading with grade 120
Sic paper. Prior to testing the coupons were stamped with an STL test number,
cleaned degreased, measured and weighed.

7.0 Test Procedure

The SSC tesk were c o n d u ~ in two Alloy C276 IOL autoclave test vessels. Each
autoclave contained four (4) four point bend specimens. The six (8) pitting tests were
conducted in a SL, Alloy C278, autoclave.

The SSC test specimens were degreased, placed in 10 litre autoclaves and immersed
in approximately 8 litres d &aerated test sobtion. The autoclaves were sealed and the
solution was deaerated further overnight using oxygen fiee nitrogen, before being
saturated with the test gas at 60%. The autoclaves were then heated to 90°C and
132% and pressuhed at the required tatat pressure of 28 bar absolute with the test
gas, allowance being made for the steam pressure at these temperatures. The test
duration was taken as 720 hours fnxn this point. Afler cornpietion of the test period, the
pH of each solution was recorded and the specimens removed from the autoclave for
examination.

The same procedure was used for the pitting teats at 132% except the total pressure of
the test gas was 4,24 bar absolute.
 28 February 2007

Serial No. 6120190

Page 1 of 10 Pages

PO NO. 258157192

CLIENT: Bweau Veritas Inspection Ltd

Parklands
82- W i h n s b Road
Didsbury
ManChester
M20 2RE

On the instructions of the client, Sheffiekf Testing Laboratories Ltd have undertaken
sutphie s€res$cracking (SSC) and pitting cartosion testing of two welded (weld and weld
repair) samples supplied by the client in accordance with Bodycote Materials Testing
Procedure No. MUCOR 1O/C22, supplied by the client.

2.0 Test Material an8 Number of Tesb

Two s m p k of Wd 12mm 25% Cr duplex sbiniess steel pipe were suppfigd, one
marked Sa)-1 Main Procedure the other marked SO-2 Repair Procedure. Tests canid out
are detailed b e k
-
Table 1 I b l ~ r t s l sand Tests