Aluminum 3003-H112: Metal Nonferrous Metal Aluminum Alloy 3000 Series Aluminum Alloy

This document provides information on the physical, mechanical, thermal, and component element properties of the aluminum alloy 3003-H112. Key facts include that it has a density of 2.73 g/cc, tensile strength between 105-150 MPa depending on thickness, an elongation at break between 8-18% depending on thickness, a modulus of elasticity of 70.0 GPa, and is comprised primarily of aluminum (96.7-98.5%) with additions of copper, iron, manganese, and other elements each typically less than 1%.

Uploaded by

Joachim Mausolf
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
330 views2 pages

Aluminum 3003-H112: Metal Nonferrous Metal Aluminum Alloy 3000 Series Aluminum Alloy

This document provides information on the physical, mechanical, thermal, and component element properties of the aluminum alloy 3003-H112. Key facts include that it has a density of 2.73 g/cc, tensile strength between 105-150 MPa depending on thickness, an elongation at break between 8-18% depending on thickness, a modulus of elasticity of 70.0 GPa, and is comprised primarily of aluminum (96.7-98.5%) with additions of copper, iron, manganese, and other elements each typically less than 1%.

Uploaded by

Joachim Mausolf
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

Aluminum 3003-H112 http://www.matweb.com/search/datasheet_print.aspx?matguid=a1534c6...

Aluminum 3003-H112
Categories: Metal; Nonferrous Metal; Aluminum Alloy; 3000 Series Aluminum Alloy

Key
UNS A93003; AA3003-H112; Al3003-H112
Words:
Vendors: No vendors are listed for this material. Please click here if you are a supplier and would like information
on how to add your listing to this material.

Physical Properties Metric English Comments


Density 2.73 g/cc 0.0986 lb/in³

Mechanical Metric English Comments


Properties
Tensile Strength, 105 - 130 MPa 15200 - 18900 psi
Ultimate @Thickness 12.7 - 50.8 mm @Thickness 0.500 - 2.00 in

115 - 125 MPa 16700 - 18100 psi


@Thickness 6.35 - 12.7 mm @Thickness 0.250 - 0.499 in
100 - 150 MPa 14500 - 21800 psi
@Thickness 50.8 - 76.2 mm @Thickness 2.00 - 3.00 in
Tensile Strength, >= 41.0 MPa >= 5950 psi
Yield @Thickness 12.7 - 50.8 mm @Thickness 0.500 - 2.00 in

>= 41.0 MPa >= 5950 psi


@Thickness 50.8 - 76.2 mm @Thickness 2.00 - 3.00 in
>= 69.0 MPa >= 10000 psi
@Thickness 6.35 - 12.7 mm @Thickness 0.250 - 0.499 in
Elongation at Break 8.0 % 8.0 %
@Thickness 6.35 - 12.7 mm @Thickness 0.250 - 0.499 in

12 % 12 %
@Thickness 12.7 - 50.8 mm @Thickness 0.500 - 2.00 in
18 % 18 %
@Thickness 50.8 - 76.2 mm @Thickness 2.00 - 3.00 in
Modulus of Elasticity 70.0 GPa 10200 ksi
Poissons Ratio <= 0.33 <= 0.33
Shear Modulus 25.0 GPa 3630 ksi

Thermal Properties Metric English Comments


CTE, linear 21.5 µm/m-°C 11.9 µin/in-°F
@Temperature -50.0 - 20.0 °C @Temperature -58.0 - 68.0 °F
23.2 µm/m-°C 12.9 µin/in-°F
@Temperature 20.0 - 100 °C @Temperature 68.0 - 212 °F
24.1 µm/m-°C 13.4 µin/in-°F
@Temperature 20.0 - 200 °C @Temperature 68.0 - 392 °F
25.1 µm/m-°C 13.9 µin/in-°F
@Temperature 20.0 - 300 °C @Temperature 68.0 - 572 °F
Specific Heat 0.893 J/g-°C 0.213 BTU/lb-°F
Capacity

Component Metric English Comments


Elements
Properties
Aluminum, Al 96.7 - 98.5 % 96.7 - 98.5 %
Copper, Cu 0.050 - 0.20 % 0.050 - 0.20 %
Iron, Fe <= 0.70 % <= 0.70 %
Manganese, Mn 1.0 - 1.5 % 1.0 - 1.5 %
Other, each <= 0.050 % <= 0.050 %

1 von 2 24.09.2020, 10:34


Aluminum 3003-H112 http://www.matweb.com/search/datasheet_print.aspx?matguid=a1534c6...

Other, total <= 0.15 % <= 0.15 %


Silicon, Si <= 0.60 % <= 0.60 %
Zinc, Zn <= 0.10 % <= 0.10 %

References for this datasheet.

Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format.
Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to
equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you
refer to MatWeb's terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.

2 von 2 24.09.2020, 10:34