QW-483 (Red) PQR No.: Tme 358

1. A guided-bend test was performed on specimen QW-462.2 with bending angles of 180 degrees and former diameters of 4 times the thickness, and the results were satisfactory per the acceptance criteria. 2. Hardness testing found hardness readings of 000 for the weld, heat-affected zone, and parent metal. 3. Additional tests including visual examination, dye penetrant examination, chemical analysis, and metallographic examination were performed and found satisfactory.

Uploaded by

Sudhir Kotkar
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as DOCX, PDF, TXT or read online on Scribd
90 views

QW-483 (Red) PQR No.: Tme 358

1. A guided-bend test was performed on specimen QW-462.2 with bending angles of 180 degrees and former diameters of 4 times the thickness, and the results were satisfactory per the acceptance criteria. 2. Hardness testing found hardness readings of 000 for the weld, heat-affected zone, and parent metal. 3. Additional tests including visual examination, dye penetrant examination, chemical analysis, and metallographic examination were performed and found satisfactory.

Uploaded by

Sudhir Kotkar
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as DOCX, PDF, TXT or read online on Scribd
You are on page 1/ 1

QW-483 (red)

PQR No.: TME 358


Tensile Test ( QW-150) – Not Applicable
Specimen No. Width (mm) Thickness (mm) Area (mm2) Ultimate Total Load (N) Ultimate Unit Type of Failure and
Stress, (Mpa) Location

Not Applicable

Guided-Bend Test (QW-160) Test Report No. Q-07512.2 DT. 00/00/0000


Figure No. Type Bending Angle Former Diameter Result
QW-462.2 Transverse side Bend 1 (Bending Angle 180 degree) 4 x t = 40mm Satisfactory (QW-163 Acceptance Criteria)
QW-462.2 Transverse side Bend 2 (Bending Angle 180 degree) 4 x t = 40mm
QW-462.2 Transverse side Bend 3 (Bending Angle 180 degree) 4 x t = 40mm
QW-462.2 Transverse side Bend 4 (Bending Angle 180 degree) 4 x t = 40mm
Toughness test (QW-160) Test Report No. Q-07512 DT.00/00/0000
Specimen No. & Notch Location Specimen Size Test Temperature Impact Values (J)
(mm) Sample 1 Sample 2 Sample 3 Average
Not Applicable
Fillet-Weld test (QW-170)-Not Applicable
Result – Satisfactory: Yes No penetration into Parent Metal: Yes No
Macro – Not Applicable

Vicker Hardness HV-10, REPORT No:Q07512.1 Dtd:00/00/0000


SR. NO. Process Location Result
1 SMAW Weld 000 000 000
2 SMAW Haz 000 000 000
3 SMAW PARENT METAL 000 000 000
OTHER TEST
Types of test
(1)Visual examination : Satisfactory WELDING WITNESS SHOP SHEET Dated.00/00/0000
(2) Dye penetrant Examination : Satisfactory WELDING WITNESS SHOP SHEET Dated.00/00/0000
(3) Chemical Analysis: Refer Annexure – 1;
(4) IGC as per Method ‘’A’’ of ASTM G28: Satisfactory
(5) Metallographic Examination of Weld, HAZ & PARENT METAL : Satisfactory
Welder’s Name: xxx Clock No. ---- Stamp No. W-000
Test conducted by: ABC PVT. LTD. Test report no.: Q-000, Q-000
We certify that the statements in this record are correct and that the test welds were prepared, Welded and tested in accordance
with the Requirement of Section IX of the ASME Boiler and pressure Vessel Code, Edition 2017.

Organization: abc PVT. LTD.


Prepared By: Certified By: Witnessed By:

Engineer (Welding) Head Welding

Page 2 of 3