PRODUCT DATA SHEET
Sikaflex® Construction
1-part polyurethane sealant for building joints
®
PRODUCT Sikaflex -Construction is a one part, moisture curing, elastic joint sealant
based on polyurethane. It is suitable for outdoor applications.
DESCRIPTION
USES
Universal joint sealing compound for building construction, e.g.
For movement joints in
Precast concrete construction
Balcony parapets
Bridge cantilevers
Retaining walls
Subways
For caulking of
Window frames and doors
Skirtings
Wall/floor joints
Shutter housings
CHARACTERISTICS / ADVANTAGES
One-component, ready for use
Good adhesion to many substrates
Excellent workability, easy to use
Can be overpainted
Non-sag
Bubble-free curing
High tear resistance
Weather resistance, excellent aging resistance
TESTS APPROVAL / STANDARDS
ISO11600, Type F, Class 20LM
ASTM C920, Type S, Grade NS, Class 25, Use NT, G, M and A
Product Data Sheet
Sikaflex® Construction
Mar. 2018, VERSION 11
1/6
PRODUCT DATA
FORM COLOURS
White, Concrete Grey, Black, Beige, Dark Amber , Quartz Grey,
Redish Brown
PACKAGING
600ml sausages, 20 ssg per box
STORAGE STORAGE CONDITIONS / SHELF-LIFE
12 months from date of production if stored properly in undamaged and
unopened original sealed packaging in cool dry conditions. Protect from
direct sunlight and frost.
TECHNICAL DATA CHEMICAL BASE
Polyurethane (moisture-curing)
DENSITY
(According to DIN 53479)
Approx. 1.3kg/ltr (colour concrete Grey)
SKINNING TIME
60 minutes (at +23°C / 50% r.h.)
CURING RATE
Approx.1.5mm/24 hours (at +23°C / 50% r.h.)
VOC DATA
VOC content (ready to use) not exceeding 250gm/litre [Type of regulated
paint under the Air Pollution Control (volatile organic compounds)
Regulation of Hong Kong: (Architectural Sealants)].
MECHANICAL / TEAR STRENGTH
PHYSICAL PROPERTIES (According to DIN 53 515)
~ 6N/mm (+23°C / 50% r.h.)
ELONGATION AT BREAK
(According to DIN 53 504)
>600% (+23°C / 50% r.h.)
SAG FLOW
(According to DIN EN ISO 7390)
0mm, very good
ELASTIC RECOVERY
(According to DIN EN ISO 7389 B)
>85% (+23°C / 50% r.h.)
Product Data Sheet
Sikaflex® Construction
Mar. 2018, VERSION 11
2/6
MOVEMENT CAPABILITY
(According to ASTM C920 TYPE S, GRADE NS, CLASS 25, USE NT, G.M. & A)
25%
SYSTEM INFORMATION
APPLICATION DETAILS CONSUMPTION / COVERAGE
Joint Width 10mm 15mm 20mm 25mm 30mm
Joint Depth 8mm 8mm 10mm 12mm 15mm
Joint length/ssg ~7.5m ~4.5m ~2.5m ~1.6m ~1.3m
JOINT DESIGN
A) Façade joints (precast concrete elements)
(According to DIN 18540/ISO 11600)
Joint distance (m) <2.0 2.0 – 3.5 3.5 – 5.0 5.0– 6.5 6.5 – 8.0
Joint width (mm) 10 15 20 25 30
Joint depth (mm) 8 10 12 15 15
B) For other, common applications:
Sealant-bead diameter (joint factor)
Width : Up to 10 mm joint width = 1 : 1
More than 10 mm joint width = 2 : 1 (min. depth 8mm)
Min. joint width for window caulking: 10 mm
All joints must be properly designed and dimensioned by the specifier and
the main contractor in accordance with the relevant standards, because
changes are not usually feasible after construction. The basis for calculation
of the necessary joint width are the technical values of the joint sealant and
the adjacent building materials, plus the exposure of the building, its
method of construction and its dimensions.
MAX. JOINT WIDTH
35 mm
MIN. JOINT WIDTH
10 mm (Joint movement is not exceeding 25%)
MAX. PERMISSIBLE JOINT MOVEMENT
25% of average joint width (expansion-contraction)
MAX. PERMISSIBLE SHEAR MOVEMENT
20% of average joint width (longitudinal or transversal to joint)
Product Data Sheet
Sikaflex® Construction
Mar. 2018, VERSION 11
3/6
SURFACE QUALITY
Clean and dry, homogeneous, free from oils and grease, dust and loose of
friable particles, cement laitance must be removed.
SUBSTRATE PREPARATION
Non porous substrates:
e.g. powder coatings etc. have to be cleaned with a fine abrasive pad and
Sika®Activator by using a clean towel / cloth.
®
After a flash off time of at least 15 min, apply Sika Primer 3 N by using a
brush.
Before sealing allow a flash off time of at least 30 min. (max. 8 hrs.).
®
For PVC use Sika Primer 215.
Before sealing allow a flash off time of at least 30 min. (max. 8 hrs.).
Porous substrates and metal:
e. g concrete, aerated concrete and cementitious renders, mortars, brick,
®
etc. have to be primed with Sika Primer 3 N by using a brush.
Before sealing allow a flash off time of at least 30 min. (max. 8 hrs.).
Important note: Primers are only adhesion promoters. They neither
substitute for the correct cleaning of the surface nor improve their strength
significantly.
Primers improve long term performance of a sealed joint.
®
For further information refer to the Sika Primer Table.
APPLICATION INSTRUCTIONS PRIMING
For the selection of the suitable primer, please consult Sika-Primer table or
our Technical Services Department.
BACK-UP MATERIAL
Soft, round or flat polyethylene profiles.
APPLICATION METHOD/TOOLS
Protect joint flanks with masking tape.
Insert back-up profile, apply primer and observe waiting time.
Apply joint sealant with hand – or air pressure gun, avoiding air
entrapment. Level sealant with trowel to concave finish.
Where necessary, smooth sealant with clean water, adding a few drops
of a synthetic detergent.
Remove masking tape before sealant has started to cure.
SERVICE TEMPERATURE
-40°C to +70°C
SUBSTRATE TEMPERATURE
+5°C to +40°C max.
Product Data Sheet
Sikaflex® Construction
Mar. 2018, VERSION 11
4/6
AMBIENT TEMPERATURE
+5°C to +40°C max.
SUBSTRATE MOISTURE CONTENT
Dry
CLEANING OF TOOLS
® ®
Clean all tools and application equipment with Sika Remover 208/Sika
Handclean immediately after use. Hardened/cured material can only be
removed mechanically.
NOTES ON APPLICATION / When smoothing the sealant, please observe that no liquid is allowed to
LIMITATIONS penetrate between sealant and joint flank.
To maintain max. movement capacity, do not overcoat joint sealant
completely, only the joint sides should be overcoated to max. 1 mm
width. Should overcoating be necessary, trials must be carried out to
check adhesion, compatibility and drying behaviour of coating.
Compatible coatings may cover the joint sides to max. 1 mm. The
compatibility must be tested according to DIN 52 452-2.
Insufficient ventilation or lack of moisture slows curing rate.
Silicone based substrates can negatively influence curing as well as
bonding properties of sealant.
Do not apply to concrete substrate treated with transparent coatings
(glazed).
Colour may be influenced by exposure to weathering, UV or chemicals.
®
Do not directly use Sikaflex Construction as a glass sealer, on bituminous
substrates, natural rubber, EPDM rubber or on building materials which
might bleed oils,plastisicers or solvents which could attack the sealant.
®
Do not use Sikaflex Construction to seal swimming pools.
®
Do not mix with or expose uncured Sikaflex Construction to substances
that may react with isocyanates, especially alcohols which are often
components within e.g. thinners, solvents, cleaning agents and formwork
releasing compounds. Such contact could interfere or prevent the cross
linking curing reaction of the material.
Not suitable for joint with water pressure or permanent water
immersion.
Before using on natural stone contact our Technical Services
Department.
Only use in good ventilated areas.
The freshly applied sealant has a smell similar to ‘ Amaretto“ until it has
fully cured(benzalehyde).
Product Data Sheet
Sikaflex® Construction
Mar. 2018, VERSION 11
5/6
VALUE BASE All technical data stated in this Product Data Sheet are based on laboratory
tests. Actual measured data may vary due to circumstances beyond our
control.
LOCAL RESTRICTIONS Please note that as a result of specific local regulations the performance of
this product may vary from country to country. Please consult the local
Product Data Sheet for the exact description of the application fields.
HEALTH AND SAFETY INFORMATION For information and advice on the safe handling, storage and disposal of
chemical products, users shall refer to the most recent Material Safety Data
Sheet containing physical, ecological, toxicological and other safety-related
data.
LEGAL NOTES The information, and, in particular, the recommendations relating to the application and end-
use of Sika products, are given in good faith based on Sika's current knowledge and experience
of the products when properly stored, handled and applied under normal conditions in
accordance with Sika’s recommendations. In practice, the differences in materials, substrates
and actual site conditions are such that no warranty in respect of merchantability or of fitness
for a particular purpose, nor any liability arising out of any legal relationship whatsoever, can be
inferred either from this information, or from any written recommendations, or from any other
advice offered. The user of the product must test the product’s suitability for the intended
application and purpose. Sika reserves the right to change the properties of its products. The
proprietary rights of third parties must be observed. All orders are accepted subject to our
current terms of sale and delivery. Users must always refer to the most recent issue of the local
Product Data Sheet for the product concerned, copies of which will be supplied on request. It
may be necessary to adapt the above disclaimer to specific local laws and regulations. Any
changes to this disclaimer may only be implemented with permission of Sika® Corporate Legal
in Baar.
FOR MORE PRODUCT NAME® INFORMATION:
SIKA HONGKONG LTD Contact Details
1507-12, 15/F, Block A, Phone: + 852 2686 8108
New Trade Plaza, Fax: +852 2645 3671
6 On Ping Street, Mail:marketing@[Link]
Shatin, N.T. Hong Kong
[Link]
Product Data Sheet
Sikaflex® Construction
Mar. 2018, VERSION 11
6/6