Fosroc Trafficguard UR100 constructive solutions

Skid resistant, waterproof, flexible and UV resistant Typical Properties

protection system for car park decks Intermediate coat
Uses Elongation
(ASTM D412) : > 300%
Trafficguard UR100 is a modified polyurethane-based traffic
Tensile Strength
deck system designed to provide an added level of protection
(ASTM D412) : 4 N/mm2
to, new and existing, heavily trafficked areas such as:
Tear Resistance
„ Car park decks (ASTM D624) : 15 N/mm
Crack Bridging ability
„ Car park ramps
(ASTMC1305) : Pass
„ Turning areas
Membrane
„ Entrance/exit areas
Elongation
„ Thoroughfares
(ASTM D412) : > 100%
Tensile Strength
Advantages
(ASTM D412) : 6.0 N/mm2
„ Flexible and tear resistant Tear Resistance
(ASTM D624) : 26.0 N/mm
„ Multi purpose
Crack Bridging ability
„ Seamless and watertight (ASTMC1305) : Pass
„ Rapid application, reliable and safe
Wear course
„ Available in a range of colours
Weathering (30days) : No change in original
(ASTM D412) appreance
Description
Corrosive Resistance : No change in original
Trafficguard UR100 is a multi-layer deck protection system (ASTM B117) appreance
comprising a primer, waterproof membrane, flexible Humidity Resistance : No change in original
Intermediate coat and UV resistant wearing course. All (Water fog exposer) appreance
components are applied in the liquid phase and react
chemically to form a tough, flexible, protective surface. Instructions for use

Surface Preparation
Technical Support
New concrete surfaces should have a minimum curing period
Fosroc offers a comprehensive technical support service to
of 28 days. Existing concrete surfaces must be prepared to
specifiers, end users and contractors. It is also able to offer
provide a clean, sound substrate. Surfaces should be clean
on-site technical assistance, an AutoCAD facility and
and dry with open capillaries, free from laitance, oil, grease,
dedicated specification assistance in locations all over the
curing compounds or other surface contaminants. All
world.
blowholes, and other surface undulations greater than 1
mm in depth, should be repaired using Nitomortar FC(B)*†.
Temperature of the substrate during application must be
between 5°C and 40°C.

Priming

Apply Trafficguard Primer to the prepared surface at a wet film

thickness of 200 microns. Whilst Trafficguard Primer is still
wet, seed with Fosroc Anti Slip Grain No. 3 at a rate of 0.4 kg/
Trafficguard UR100

m2 and allow to cure for 24 hours.

Fosroc Trafficguard UR100
Application
Note: Varying thickness outside the normal range is possible
Membrane with each layer based on special requirements/specifications,
subject to the prior approval from local Fosroc office.
Apply Trafficguard Membrane to the primer surface at a wet film
thickness of 750-900 microns. For best results Trafficguard
Storage - Shelf life
UR100 Membrane should be applied with a notched trowel or
squeegee. Allow to cure for 16 hours at 25ºC. When stored in warehouse conditions at less than 25°C,
Trafficguard UR100 will have a shelf life of 12 months. Avoid
Intermediate Coat
storage of material under direct sunlight.
Apply Trafficguard Intermediate Coat to the membrane at a
wet film thickness of 400-750 microns. For best results the Limitations
Trafficguard Intermediate Coat should be applied with a
notched trowel or squeegee. Broadcast with Antislip Grain - Do not use on floors where rising dampness or a potential
No. 2 or 3 at a minimum rate of 2 to 3 kg/m2 and roll with Spike osmosis problem may exists.
Roller to required finish. Allow to cure for 16 hours at 25ºC. - Do not proceed with application if precipitation is imminent,
Wear Course or temperatures are expected to drop below 7°C within 24
hours of application.
Apply Trafficguard Wear Course to the Intermediate coat at
wet film thickness of 250-400 microns, which can be achieved Precautions
by multiple application. When application is complete the
system should be permitted to cure for 72 hours @ 35°C or 7 Health and safety
days @ 25°C prior to being trafficked. Trafficguard Primer, Membrane, Intermediate Coat, Wear
Cleaning Course and Fosroc Solvent 102 should not come in contact
with skin or eyes, nor should they be swallowed. Avoid
Tools and equipment should be cleaned immediately after inhalation of vapours and ensure adequate ventilation.
use with Fosroc Solvent 102*.
Wear suitable protective clothing, gloves and eye/face
Estimating protection. Use goggles, in case of accidental eye
contamination, rinse immediately with plenty of water and
Supply seek medical advice. If swallowed seek medical attention
Trafficguard Primer : 9 litre packs immediately - do not induce vomiting.
Trafficguard membrane : 8 litre packs
Fire
Trafficguard Intermediate Coat : 18 litre packs
Trafficguard Wear Course : 20 litre packs Fosroc Solvent 102 is flammable. Do not use near a naked
Antislip Grains No. 2, 3 : 25 kg bags flame.

Coverage Flash points

Trafficguard Primer : 5 m2/litre Fosroc Solvent 102 : 33°C
Trafficguard membrane : 1.1 to 1.3 m2/litre
For additional information see relevant Material Safety Data
Trafficguard Intermediate Coat : 1.3 to 2.5 m2/litre
Sheet.
Trafficguard Wear Course : 2.5 to 4 m2/litre

* Denotes the trademark of Fosroc International Limited

†
See separate data sheet
Important note
Fosroc products are guaranteed against defective materials and manufacture and are sold subject to its standard Conditions for
the Supply of Goods and Service. All Fosroc datasheets are updated on a regular basis. It is the user’s responsibility to
obtain the latest version.

Head Office
telephone: (+9714) 2039699 fax: (+9714) 2859649 email: [email protected]
Al Gurg Fosroc LLC
Regional offices
Post Box 657, Dubai Abu Dhabi, Al Gurg Fosroc telephone: 673 1779 fax: 673 1449 email: [email protected]
United Arab Emirates Bahrain, YBA Kanoo telephone: 17738200 fax: 17732828 email: [email protected]
Kuwait, Boodai telephone: 4817618 fax: 4832124 email: [email protected]

www.fosroc.com
Oman, Al Amana telephone: 24815080 fax: 24817554 email: [email protected]
Qatar, Tadmur telephone: 4665501 fax: 4664147 email: [email protected]

UAE/0374/10/I