The document discusses welding procedure qualification requirements according to AWS and ASME codes. It begins by defining a Welding Procedure Specification (WPS) and Welding Procedure Qualification Record (PQR). It states that a WPS must be developed first, then a PQR performed to qualify the procedure. A PQR involves mechanical testing of test welds to demonstrate the contractor's ability to make welds according to the WPS. Finally, Welder Performance Qualification Tests (WPQT) are conducted to qualify individual welders to make production welds using the qualified procedure.

Uploaded by

wenigma
Copyright
© © All Rights Reserved
Available Formats
Download as PPSX, PDF, TXT or read online on Scribd
248 views

Code Presentation

The document discusses welding procedure qualification requirements according to AWS and ASME codes. It begins by defining a Welding Procedure Specification (WPS) and Welding Procedure Qualification Record (PQR). It states that a WPS must be developed first, then a PQR performed to qualify the procedure. A PQR involves mechanical testing of test welds to demonstrate the contractor's ability to make welds according to the WPS. Finally, Welder Performance Qualification Tests (WPQT) are conducted to qualify individual welders to make production welds using the qualified procedure.

Uploaded by

wenigma
Copyright
© © All Rights Reserved
Available Formats
Download as PPSX, PDF, TXT or read online on Scribd
You are on page 1/ 60

American Welding Society

Nashville Section
Welding Procedure Development

AWS & ASME


Welding Procedures

Welding Procedure
Specification (WPS)

Written document that provides direction to


the welder for making production welds in
accordance with Code requirements
Rules for qualification of procedures vary by
referencing Code
Qualified by testing (ASME, AWS)
Pre-qualified (AWS)
Standard Welding Procedure Specification (AWS)

AWS Standard Welding Procedure


Specification (SWPS)
Procedures that have been qualified by
the Welding Research Council accepted
and published by AWS for use as a
qualified welding procedure
ASME and NBIC accepted procedures
are listed in the appendix of the
applicable Code

Welding Procedure
Qualification (PQR)

A test that is performed to demonstrate that


the contractor can make satisfactory welds as
specified in the Welding Procedure
Specification
Mechanical testing is required and NDE may
be required, depending on the Code being
qualified to
Impact testing may be required by the
referencing Code (i.e., ASME Sect VIII)

Welder Performance
Qualification Test (WPQT)

Performance test which determines the welders


ability to make acceptable production welds under a
given set of conditions (essential variables)

Process
Joint type
Base metal
Filler metal
Position
Gas
Electrical characteristics

Which Comes First


WPQT

WPS

PQR

Which Comes First


To frame a house you need to know the
size of the foundation
To build a foundation you need to know
the size and shape of the house

Which Comes First

The roof does not have to cover the


house but should be fully supported by
the framing

The Welding House

The WPS and the PQR are developed


concurrently
Rough draft the WPS to determine how to do the
PQR(s)
More than one PQR may be required to fully
support the WPS (e.g., thickness range)
Welder qualification tests should be designed to
not exceed the limits of the WPS but do not need
to meet all of the limits of the WPS

AWS B2.1

Specification for Welding Procedure and


Performance Qualification
Base metals categorized in M number format
Similar to ASME P numbers
Similar to ASME Section IX

ASME B&PV Code

ASME B&PV Code Section IX contains


the guidelines for welding procedure and
welder qualification
Requires procedure qualification for all
welding procedures except when the
contractor has adopted one of the AWS
Standard Welding Procedure Specifications

AWS Codes

Many AWS Codes allow the use of Prequalified Welding Procedures


Pre-qualified procedures are written documents
that define welding parameters for the welder and
are within defined limits set by the referencing
Code (e.g., AWS D1.1)
Welding procedures that exceed the limits for prequalification must be qualified by testing

Develop the WPS

Process(es)
Material(s)
Material thickness
Joint design
Filler metal
Weld deposit
thickness

Positions

Pre-heat

Post heat

Shielding gas

Electrical
characteristics

Technique

Qualify or Not to Qualify


Does the Code allow use of a prequalified procedure?
Does the planned WPS stay within the
limits of a pre-qualified procedure?

Process, joint type, material, filler metal,


position, deposit thickness

What is in the WPS

The WPS should describe all essential,


non-essential and when required by the
referencing Code supplementary
essential variables for each welding
process

Essential Variables
Essential variables are those variables in
which a change, as described in the
specific variables, is considered to affect
the mechanical properties of the
weldment
If there is a change in the essential
variable the procedure must be requalified

Supplementary Essential
Variables

Supplementary essential variables are required for


metals for which other Sections or Codes specify
notch-toughness testing and are in addition to
essential variables for each process
This means that when ASME Section VIII (which requires
qualification to Section IX) also requires notch toughness
testing on a material, the supplementary essential variables
become essential variables for that WPS
A change in either essential or supplementary essential
variables requires re-qualification of the procedure

Nonessential Variables

Nonessential variables are those in


which a change, as described in the
specific variables, may be made in the
WPS without re-qualification

Qualifying a procedure

Determine what the required essential and if


applicable supplementary essential variables are for:

Process
Joints
Base metals
Filler metals
Positions
Pre & post weld heat treatment
Gas
Electrical Characteristics
Technique

SMAW Variables (ASME Sect IX)

Welding Data
(ASME Sect IX)

The welding variables table refers to the


paragraph in the welding data section of
the Code
These paragraphs give rules for specific
applications (specific variables)

Welding Data
(ASME Sect IX)

Planning the PQR

Plan your PQR to give you the greatest


possibility of success!
Base metal and filler metal grouping
Thickness limitations
Multiple processes require addressing
essential variables for both processes
Note that position is not an essential variable
unless notch toughness testing has been
required, take advantage of that

Base Metal

Assigned P numbers (M or S) so that similar


base metals may be qualified by testing one
base metal in the same P number (essential
variable)
Group numbers may be assigned within a P
number to further differentiate
(supplementary essential variable)
SA-106 Grade B > P-No.1, Group-No.1
60 KSI min specified tensile

SA-106 Grade C > P-No.1, Group-No.2


70 KSI min specified tensile

Filler Metals

F number
Electrodes and weld rods are grouped to reduce
the number of welding procedure and
performance qualifications where it can be
logically done

A number
Classification of ferrous weld metal analysis

Product Form
Flux cored
Bare (solid) or metal cored
powder

Preheat

Decrease > 100F


Essential variable

Increase > 100 F


Supplementary essential variable

Post Weld Heat Treatment

PWHT
Essential variable

PWHT (Time & Temp range)


Supplementary essential variable

Base metal thickness (T) limits


Essential variable

QW-407.1 A separate PQR is required for


each of the following conditions.

For P-Nos. 1,3,4,5,6,9,10 & 11


No PWHT
PWHT below the lower transformation temp
PWHT above the upper transformation temp
normalizing

PWHT above the upper transformation temp followed by


HT below the lower transformation temp
Normalizing or quenching followed by tempering

PWHT between the upper and lower transformation temp

QW-407.1 contd

For all other materials


No PWHT
PWHT within a specified temperature range

Test Plate or Pipe Joint

1G position when
possible (Flat)
Plan sequence of weld
passes if multi pass
Back grind and PT if two
sided weld
Grind stops and starts

PQR Test Coupons


Reduced
Tensile
Root or
Side Bend

Root or
Side Bend
Discard

Discard
Face or
Side Bend
Face or
Side Bend

Reduced
tensile

Two Birds With 1 Stone

The Procedure Qualification and Welder


Qualification can be done at the same time
Plate 1G
Pipe 6G

Tests required for Procedure Qualification


Bend
Tensile
Notch Toughness if required by referencing Code

Read The Notes!

Required Testing for PQR


(ASME Sect IX)

Pre-qualified WPS

May be written to perform a specific weld within a


limited range of variables

One joint design (i.e., V-Groove with backing)


Material thickness limited or un-limited
Process (i.e., SMAW)
Position may be limited or all position
Current and voltage range limited

May be written to perform multiple welds, taking


advantage of a broad range of materials, joint types,
positions, etc.

AWS D1.1 Pre-qualified WPS

AWS D1.1 Pre-qualified WPS

AWS D1.1 Pre-qualified


joint design

Notes

Notes

Pre-qualified Base Metals

Pre-qualified pre-heat table

Notes for base metals


and pre-heating

Not
pre-qualified

Welder Qualification
Essential Variables

Joints
With or without backing

Base metal
Pipe diameter
P number

Welder Qualification
Essential Variables

Filler metal
With or without
F number
Inserts
Solid or metal cored
t of deposit
t limits of short circuiting transfer

Welder Qualification
Essential Variables

Position
Flat
Horizontal
Vertical
Overhead

Progression vertical welding


Up
Down

Welder Qualification
Essential Variables

Gas
Deletion of inert backing gas

Electrical characteristics
GMAW transfer mode
GTAW current or polarity

Welder Qualification

Main controlling factors


Process
Filler metal
P number qualified
It is your responsibility to ensure that the filler
metal and base metal are suitable for the
application

Welder Qualification
Base Metal
Test on pipe or plate?
Any P-No. 1 through 11, P-No. 34, or PNo. 41 through 47 qualifies for any PNo. 1 through 11, P-No. 34, or P-No. 41
through 47 base metal
P-No. 21 through P-No. 25 (same)
P-No. 51 through P-No. 53 or P-No. 61
through P-No. 62 (same)

Welder Qualification
F-Numbers

Some cross qualification exists with F


numbers for example
Any F6 qualifies for F6
Any F21 F25 qualifies for F21 F25
Any F34 or F41 F47 qualifies for F34 &
F41 - F47

Welder Qualification
F-Numbers

SMAW electrode F numbers 1 4 are


inter-related (ASME) and with or
without backing applies
F4 without backing qualifies for F1, F2, F3
& F4 with backing and F4 without
F4 with backing qualifies for F1, F2, F3 &
F4 with backing only

Welder Qualification
Weld Deposit t

ASME
Up to and including 3/8 thick qualifies 2t
Over 3/8 qualifies 2t
1/2 & over with minimum of 3 layers of weld
metal qualifies for the maximum to be welded

AWS D1.1
1/8 t 3/8 qualifies for 2t
3/8 < t < 1 qualifies for 2t
1 and over qualifies for unlimited

Welder Qualification
Position (ASME)

1G plate qualifies
F plate & pipe 2 7/8 OD & over groove
welds and F fillets

2G plate qualifies
F & H plate & pipe 2 7/8 OD & over
groove welds and F & H fillets

Welder Qualification
Position (ASME)

3G plate qualifies
F & V plate & pipe groove welds 24 OD &
over and F, H, V fillets
F pipe 2 7/8 OD & over groove welds

4G plate qualifies
F & O plate & pipe groove welds 24 OD &
over and F, H, O fillets
F pipe 2 7/8 OD & over groove welds

Welder Qualification
Position (ASME)

1G pipe
F groove & fillet

2G pipe
F & H groove & fillet

5G pipe
F, V & O groove & fillet

2G & 5G pipe or 6G pipe


All groove & fillet

Welder Qualification
(ASME)

Diameter limits based on OD of test coupon


for groove welds
< 1 OD = size welded to unlimited
1 < 2 7/8 OD = 1 OD to unlimited
2 7/8 OD & over = 2 7/8 OD to unlimited

Groove weld test qualifies fillets for all base


material thickness, sizes and diameters

Welder Qualification

Most testing can be done on carbon steel


test coupons to save money
e.g., welder qualifications can be completed
for most nickel alloys by using a filler from
the F-41 through F-47 group welding a
carbon steel test coupon

6G pipe position is the most economical


test position

Qualification by Workmanship
Test

Only permitted when allowed by the


referencing document
Requires completion of a workmanship test
addressing typical production joints and
conditions
Primarily accepted on the basis of visual
inspection
Other tests or examinations may be required
by the referencing document (e.g., macro
examination)

Continued Qualification

ASME, AWS (except D9.1) requires that the


welder must satisfactorily weld using the
process at least once each six months to
remain qualified
D9.1 is 12 months

Re-qualification may be done on pipe or plate


in any position, material thickness or
diameter to regain qualification for all
positions, thickness, materials and diameters
previously qualified for with that process