Vipel F013 Series Bisphenol A Epoxy Vinyl Ester Resins

Product Information

Vipel Corrosion Resistant Bisphenol A, Epoxy Vinyl Ester Resins


TYPICAL PROPERTIES OF CURED RESIN* (1)

Test Units of Measure Tensile Strength, psi/MPa Tensile Modulus, psi/GPa Tensile Elongation, % Flexural Strength, psi/MPa Flexural Modulus, psi/GPa Heat Distortion Temp. F/C @ 264 psi Barcol Hardness, Ultimate

Nominal 12,800/88 470,000/3.2 6.6 21,800/150 530,000/3.7 232/111 34

Test Method ASTM D 638 ASTM D 638 ASTM D 638 ASTM D 790 ASTM D 790 ASTM D 648 ASTM D 2583 BENEFITS Versatile
Wide formulating capabilities allow for use in many processes and for optimization of cost/performance.

TYPICAL LIQUID RESIN PROPERTIES* (2) see back page

GEL TO PEAK STYRENE PEAK VISCOSITY THIX GEL TIME EXOTHERM EXOTHERM SPECIFIC CONTENT VERSION INDEX minutes % F/C GRAVITY minutes cps NA 232 18 359/182 1.04 45 F013-AAA-00 3501 F013-AAB-00 F013-HHH-00
1) 2) 3) 4)

Unique composition produces a tough and versatile resin with excellent crack and craze resistance in molded parts. Vipel F013 is suitable for moldings that are subjected to particularly high static or dynamic loads, such as pipe, tanks, duct work and flooring applications. Vinyl ester resins have excellent resistance to sustained heat.

4501 3200
4

NA NA

232 16
3

18 10

350/177 302/150

1.05 1.08

43 33

77F/25C Brookfield RV viscosity spindle 2 at 20 rpm 77F/25C Gel time with 0.1% cobalt 6%, 0.1% DMA and 1.25% MEKP 77F/25C Gel time with 0.25% cobalt 6%,and 1.25% MEKP 77F/25C Brookfield RV viscosity spindle 3 at 20 rpm

Corrosion Resistant Vipel F013 highly resistant to hydrogen peroxide, and alkalis, and performs well in DESCRIPTION various stages of hypochlorite and chloAOCs Vipel F013 series is a bisphenol A epoxy-based vinyl ester resin dissolved in rine production. Refer to AOC for corrostyrene. The Vipel F013 series is ideally suited for use in hand lay-up, spray-up, sion resistance information or for quesfilament winding and pultrusion processes where outstanding mechanical properties and tions regarding suitability of a resin to any excellent resistance to chemicals and heat are required. particular chemical environment.
*Typical properties are not to be construed as specifications.

Food and Drug All resins in this datasheet are manufactured from raw materials that are listed in FDA regulation Title 21 CFR 177.2420. It is the fabricators responsibility to also be sure that the final composite is well cured. All composites used for FDA applications should be post cured at 180F/82C for at least 4 hours. After post curing it should be washed with soap and water and rinsed.

Vipel F013 Series Bisphenol A Epoxy Vinyl Ester Resins


VIPEL F013 -A SERIES GEL TIMES 1.25% MEKP AT 25C/77F

Notes: Do not decrease Aniline below DMA 0.1% or DEA 0.2% 0.2% Diethyl Aniline may be substituted for 0.1% DMA

Formulation

0.1% Cobalt 6% 0.1% DMA**

Gel Gel to Peak 2, 4-P * % Time Peak Exotherm minutes minutes F/C 0 23 18 359/182 0.025 35 18 351/177 0.05 66 28 346/174 0.075 117 32 333/167 0.1 173 35 321/161

* 2,4-Pentandione ** N, N-Dimethylaniline

PERFORMANCE GUIDELINES A. Keep full strength catalyst levels between 1.0% - 2.0% of the total resin weight. B. Maintain shop temperatures between 65F/18C and 90F/ 32C and humidity between 40% and 90%. Consistent shop conditions contribute to consistent gel times and will help the fabricator make a high quality part. C. Finished part surfaces that have been cured at room temperature in contact with air should be relatively tack free. They may not, however, be fully cured and are thus not as resistant to chemicals as a fully cured part. If no further laminating is planned, a 10% solution of 5% paraffin wax solution (MP 115118F/46-48C) in styrene may be added to the last resin layer to provide a tack free surface. D. Optimum cure and performance may be obtained by post curing room temperature cured laminates for two hours at 158212F/70-100C. E. Room temperature curing by means of cobalt acceleration should be completed with low hydrogen peroxide content MEKP catalyst to minimize foaming. SAFETY See appropriate Material Safety Data Sheet for guidelines.

ISO 9001:2008 CERTIFIED The Quality Management Systems at every AOC manufacturing facility have been certified as meeting ISO 9001:2008 standards. This certification recognizes that each AOC facility has an internationally accepted model in place for managing and assuring quality. We follow the practices set forth in this model to add value to the resins we make for our customers. STORAGE STABILITY This product is stable for seven months from the date of manufacture when stored in the original containers, away from direct sunlight or other UV light sources and at or below 25C. After extended storage, some drift may occur in the product viscosity and gel time. FOOTNOTES (1) Based on tests of Vipel F013-AAA-00 at 77F/25C. and 50% relative humidity. All thixotropic resins should be mixed well prior to use. The use of thixotropy degrades the corrosion performance of a resin in some chemical environments such as sodium chloride. All tests on unreinforced cured resin. Castings were post cured. (2) The gel times shown are typical but may be affected by catalyst, promoter, inhibitor concentration, resin, mold, and shop temperature. Variations in gelling characteristics can be expected between different lots of catalysts and at extremely high humidities. Pigment and/or filler can retard or accelerate gelation. It is recommended that the fabricator check the gelling characteristics of a small quantity of resin under actual operating conditions prior to use.

North America [email protected] Toll Free: +1 (866) 319-8827 www.aoc-resins.com

Global Contacts
Australia [email protected] Middle East [email protected] Latin America [email protected] Africa [email protected] Asia [email protected] Europe [email protected]

The information contained in this data sheet is based on laboratory data and field experience. We believe this information to be reliable, but do not guarantee its applicability to the users process or assume any liability for occurrences arising out of its use. The user, by accepting the products described herein, agrees to be responsible for thoroughly testing each such product before committing to production. Our recommendations should not be taken as inducements to infringe any patent or violate any law, safety code or insurance regulation.

Pub. No. NA-T- AOC-Vipel F013 Series