Material/Product Specification Extrusions PPS 3010/42

This document provides material specifications for extruded PPS 3010/42 plastic, including required values for various tests of its tensile strength, elongation, modulus, density, and resistance to factors like heat, tracking, water absorption, corrosion, and abrasion. The specifications establish minimum or maximum acceptable levels of performance for the material to pass qualification testing.

Uploaded by

Horacio Berni
Copyright
© Attribution Non-Commercial (BY-NC)
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
150 views2 pages

Material/Product Specification Extrusions PPS 3010/42

This document provides material specifications for extruded PPS 3010/42 plastic, including required values for various tests of its tensile strength, elongation, modulus, density, and resistance to factors like heat, tracking, water absorption, corrosion, and abrasion. The specifications establish minimum or maximum acceptable levels of performance for the material to pass qualification testing.

Uploaded by

Horacio Berni
Copyright
© Attribution Non-Commercial (BY-NC)
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

Material/Product Specification

Test

Extrusions

PPS 3010/42

Spec. Quality Clause Assurance 4.3 4.3 4.4 Product Acceptance Product Acceptance Product Acceptance

Requirement S.I. Units 10 MPa min. 200% min.

Requirement Imperial Units 1450 PSI min. 200% min.

Tensile Strength Ultimate Elongation Secant Modulus (232)C Low Temperature Secant Modulus (03)C Secant Modulus (803)C Density Accelerated Ageing 168 hrs. at (1502)C - Tensile Strength - Ultimate Elongation Thermal Endurance Dielectric Strength 1.27mm/0.050 inch wall Volume Resistivity Dielectric Constant Tracking and Erosion Resistance

103 MPa min. 4.4 Qualification 445 MPa max.

15000 PSI min. 65000 PSI max.

4.4

Qualification 103 MPa min. 15000 PSI min. (1.15 - 1.35) g/cm3

4.5 4.9

Product Acceptance Qualification

(1.15 - 1.35) g/cm3

10 MPa min. 100% min. 4.11 4.30 Qualification Qualification 217 kV/cm min. 4.31 4.32 4.33 Qualification Qualification Qualification 1x1013 Ohm cm min. 5.0 max. No tracking or erosion to top surface or flame failure after: 1 hr at 2.50kV 1 hr at 2.75kV 1 hr at 3.00kV 20 min at 3.25kV 1% max. 105C min.

1450 PSI min. 100% min. 105C min.

550 V/mil min. 1x1013 Ohm cm min. 5.0 max. No tracking or erosion to top surface or flame failure after: 1 hr at 2.50kV 1 hr at 2.75kV 1 hr at 3.00kV 20 min at 3.25kV 1% max.

Water Absorption 336 hrs. at (232)C Resistance to Bird Excrement 168 hours at (602)C - Tensile Strength - Ultimate Elongation

4.40

Qualification

4.41

Qualification 10 MPa min. 100% min. 1450 PSI min. 100% min.

Note: Secant modulus test specimens to be cut in the direction transverse to the direction of extrusion. Tensile/Elongation Test Speed: A

Raychem Electrical Products Division

Specification Guide 1 Section 3

Effective: 4/99 Supersedes: none Revision: none

Material/Product Specification
Test

Extrusions

PPS 3010/42

Spec. Quality Clause Assurance 4.41 Qualification

Requirement S.I. Units

Requirement Imperial Units

Resistance to Cable Grease 168 hours at (602)C - Tensile Strength - Ultimate Elongation Corrosive Effect 16 hrs. at (1352)C Low Temperature Impact at -(202)C Abrasion Resistance 1000 cycles, 2067,4 g weight, K6 carbide blank blade

10 MPa min. 100% min. 4.43 Qualification No corrosion

1450 PSI min. 100% min. No corrosion

4.45

Qualification

No cracking

No cracking

4.46

Qualification

20% max. thickness loss

20% max. thickness loss

Note: Secant modulus test specimens to be cut in the direction transverse to the direction of extrusion. Tensile/Elongation Test Speed: A

Raychem Electrical Products Division

Specification Guide 1 Section 3

Effective: 4/99 Supersedes: none Revision: none