Mech 423 #2

1
General design rules
for riser necks used in
iron castings;
a. general riser
b. side riser for plates
c. top round riser
Risers and Riser Design
Mech 423 #2
2
Figure 5.10 (a) Castings with blind feeders, F2 is
correctly vented but has mixed results on sections S3
and S4. Feeder F3 is not vented and therefore does
not feed at all. The unfavourable pressure gradient
draws liquid from a fortuitous skin puncture in
section S8. The text contains more details of the
effects. (b) The plastic coffee cup analogue: the
water is held up in the upturned cup and cannot be
released until air is admitted via a puncture. The
liquid it contains is then immediately released.

Gating System Design
Mech 423 #2
3
A - gates
B - runner
C - Sprue exit (Choke)
System is often designed to
follow ratio of (CSA) 1:2:2, or
1:4:4 WRT:
Sprue exit CSA C : total runner
CSA B: total gate CSA A
Gating system is un-pressurized
if area is increasing (e.g. 1:4:4)
or pressurized if there is a
constriction (4:8:3).
Gating System Design
Un-pressurized system reduces
metal velocity and turbulence
Pressurized systems usually
reduce size and weight of gating
system (pressure at constriction
(gate) causes metal to completely
fill runner more quickly)
Lecture 3
4
Lecture 3
Expendable Mould Casting
MECH 423 Casting, Welding,
Heat Treating and NDT
Credits: 3.5 Session: Fall
Time: _ _ W _ F 14:45 - 16:00
2 types of Casting Process -
Expendable & Reusable Mould
Expendable mould requires pattern
Similar to final product
Modified in dimension based on material
and process
Shrinkage allowance (pattern to be
larger than part at room temp)
Done by using shrink rules which take
into account the shrinkage allowance (1
will be 1 3/16 in a shrink rule for brass)
Patterns Shrink Allowance
Lecture 3
6
Facilitate withdrawal from mould,
patterns may be split at parting line
Location of parting line important -
the plane at which 1 section of the
mould mates with other section(s)
Patterns Draft
Flat line is preferred, but casting design and
mould may require complex parting lines
To effect withdrawal Draft is given
Depends on mould material and procedure
1/8
th
to 1/16
th
of an inch per feet is standard
Can be reduced by increasing mould
strength and automatic withdrawal
Lecture 3
7
Good castings require good
design.
Simple, simple, simple!
Communicate with foundry.
Location of Parting Plane -
effect:
number of cores
use of effective gating
weight of final casting
method of supporting cores
final dimensional accuracy
ease of moulding.
Minimize cores if possible.
Patterns Parting Line
Lecture 3
8
Machining Allowance is given on pattern for final finishing operations in
casting
Depends on the mould process and material
Sand castings rougher than shell castings
Die, investment castings are smooth, no machining required
Patterns Allowance
Designer needs to look into these
before deciding the final
machining allowance required
Sometimes draft can serve to act
as part or whole of machining
allowance
Lecture 3
9
Patterns Cores
Cores to be big to compensate for shrinkage
Core prints to be added in pattern
Machining allowance to be reduced from core
Size machining increases hole size
Lecture 3
10
Patterns Allowances
Distortion allowance
U shape castings will distort by bending
outside
To prevent this patterns to be made with
an inward angle
Long horizontal pieces sag in the centre if
adequate support not given
If casting is done directly from reusable mould, all these allowances
should go into the mould cavity
In addition, heating of metal moulds and its expansion while in
operation should be taken into account before deciding the final size
Lecture 3
11
13-13 Elimination of core
by changing parting line.
Also eliminates draft which
reduces weight
Design Consideration in Castings
Good quality at lowest possible cost.
Attention to common requirements
Changes in design to simplify casting
example - Location of Parting Plane
can affect:
number of cores
use of effective gating
weight of final casting
method of supporting cores
final dimensional accuracy
ease of moulding.
Minimize cores if possible.
Lecture 3
12
Design Consideration in Castings
Cores can also be eliminated by
design change
Design dictates location of patterning
plane - cannot be on the plane of
round edges
Draft also can determine the parting
plane giving it as a note provides
more options in foundry
Lecture 3
13
Sections with high area to volume ratio will cool faster.
Heavier sections cool slower - more potential for void formation
on solidification, and large grains.
Try for uniform wall thicknesses.
If not possible use gradual changes in section
Design Consideration in Castings
Lecture 3
14
Where walls/sections intersect - problems.
Stress concentrations (use fillets)
Hot spots. Localized thick section at
intersection (especially if fillets too big!).
These regions cool slower and often contain
voids.
Try to avoid hot spots and voids in castings.
Sometimes use cores to make deliberate,
controlled voids in heavy sections.
Place risers to feed heavy sections/hot spots.
Stagger ribs on plates to avoid high
stresses/cracking.
Design Consideration in Castings
Lecture 3
15
Use risers near heavy sections.
Adjacent riser feeds these sections
Shrinkage will be in the riser that will
be cut off rather than in the casting
Intersecting Sections crack.
When ribs are placed, due to
shrinkage, material cracks at the
intersection
Possible solution is to use staggered
ribs arrangement.
Design Consideration in Castings
Lecture 3
16
Design Consideration in Castings
Avoid large, unsupported areas - tend to warp on cooling disrupts
smooth surface (especially if reflective)
Consider location of parting line
Flash often appears at parting line
Locate parting line at corners/edge rather in middle
Consider minimum thickness. Use common sense and ask advice
Lecture 3
17
Expendable Mould Casting
Lecture 3
18
1. Single use moulds made from the same pattern (multiple-use
pattern)
2. Single use moulds made from single-use patterns (one-off).
These two are called expendable mould casting processes
Mould material usually made from sand, plaster, ceramic
powder mixed with binder.
Metals often cast this way are: iron, steel, aluminum, brass,
bronze, magnesium, some zinc alloys, nickel-based alloys.
Cast iron and aluminium are most common:
Cheap, good fluidity
low shrinkage, good rigidity,
Good compressive strength and hardness
Introduction
Lecture 3
19
Most common casting technique
Sand (mixture of sand + clay + water) is
packed around pattern.
Pattern removed to give cavity, sprue,
runners added
Mould closed, metal poured in.
After solidification, sand broken out and
casting removed. Casting fettled.
New mould required for next casting
(Expendable moulding).
Sand Casting
Lecture 3
20
For most expendable mould casting techniques a pattern is required
Material depends on No. of castings to be made, metal being cast,
process being used, size and shape, dimensional precision required
Multiple - Use Patterns
Wood - Cheap, easily machined but prone to warping, swelling
(moisture), unstable, wears. Used for small runs.
Metal - more expensive but stable, accurate, durable. Typically
aluminium, cast iron or steel. Either cast then machined or
machined directly (e.g. NC-machining). Large runs and elevated
pressure and/or temperature moulding process
Patterns and Pattern Materials
Lecture 3
21
Plastic - Epoxy and Polyurethane. More common now. Easy
preparation, stable and durable relative to wood. Cast &
machined, easily repaired, can be reinforced/backed
Expendable (single-use) patterns:
Wax - used for investment casting. Wax formulated for
melting point, viscosity, ash residue etc. Melted out (mostly)
before casting
EPS - Expanded PolyStyrene. Pre-expanded beads blown
into mould, heated (steam) to completely fill mould and bond
beads. Pattern is burnt out by molten metal. Carbon film
possible.
Patterns and Pattern Materials
Lecture 3
22
Types of Pattern
Type of pattern depends on number of castings and
complexity.
One Piece (Solid) Patterns - simplest, cheapest, slowest
moulding. For simple, low number of castings.
Only allowances and core prints
Split Patterns - splits into two parts where
parting line will be.
Mould drag first with bottom part of pattern,
invert, add top half of pattern (locating pins)
then mould cope.
Remove pattern, close, cut runner, riser etc
and ready to pour.
OR each part of the mould (Cope & Drag)
can be moulded separately then joined
High volume and large castings
Types of Pattern
Lecture 3
24
Match-Plate Patterns - a plate with the cope pattern
on one side and the drag pattern on the other side
(with locating pins and holes respectively).
Can include runners and gates. Made from wood and
joined or machined/cast from metal. (higher volumes,
small to medium size castings).
Types of Pattern
Lecture 3
25
Loose Piece Patterns - Special patterns can be made for very complex
shapes. Pattern is assembled from different pieces held together with
pins. Pieces are withdrawn sequentially after pin removed. Expensive.
All patterns should have a small radius on internal corners to prevent
stress concentrations in the casting, avoid shrinkage cracking and make
pattern easier to remove without mould damage
(3-7mm is good). Machined in for NC patterns;
added to patterns using wax, plastic strips.
Types of Pattern
Lecture 3
26
SAND - very important part of sand-casting. Require following
properties.
Refractoriness - ability to withstand high temperatures.
Silica (sand)- cheap, lower temps (Al, Mg possibly cast
iron).
Zircon (ZrO2.SiO2) - more expensive, higher temps. Steels.
Investment casting.
Others
Cohesiveness - how well the sand bonds together to give
shape.
Controlled by adding binder, clays (bentonite, kaolinite) +
water.
Sand and Sand Conditioning
Lecture 3
27
Permeability - ability to allow gas to pass through/escape as
metal fills cavity. Denser packing - stronger, better surface
finish but less permeability.
Depends on size and shape of sand particle, amount of clay
and water, compacting pressure.
Collapsibility - ability to permit metal to shrink after solidification
and also to disintegrate during knock-out.

Usually trade-off in properties: more clay means stronger bond
but less permeability and refractoriness etc.
88% Silica, 9% clay, 3% water; typical for green-sand cast.
Blended and mixed; uniform, flows easily into mould (Fig 14-8)
Tested for grain size, moisture content, permeability, strength
etc.
Sand and Sand Conditioning
Lecture 3
28
Grain Size tested by shaking in 11 sieves of decreasing mesh
size and the weight in each of them gives an idea of grain size.
Moisture electrical conductivity, or weigh 50g sample of sand
after heating for sometime at 110C for water to evaporate
Clay wash 50g of sample sand with alkaline water (NaOH) to
remove clay, dry the sand and weighed to find the clay content
Permiability measure of escape gases done by standard
ramming of sand and passing air through it at known pressure.
Pressure loss between orifice and sand gives permiability (12-9)
Compressive Strength also mould strength. Use the prepared
sample and compressively load it find when it fails
Hardness Resistance of sand to spring loaded steel ball (12-10)
Compactibility 45% is good. Amount of height change from
loose sand to application of standard load
Sand Testing
Lecture 3
29
Round grains - better
permeability, minimize clay
required.
Angular grains - better
strength due to interlocking.
Sand Properties and Defects
Large grains - better permeability, better high temps.
Smaller grains - better surface finish.
Uniform particle size - better permeability.
Wide PSD - better strength & surface finish.
Sand expands on heating; (also phase transformation in silica).
Expands next to cavity but not elsewhere, sometimes get sand
expansion defects especially on long flat surfaces.
Lecture 3
30
Sand expands on heating; (also phase transformation in silica).
Expands next to cavity but not elsewhere, sometimes get sand
expansion defects especially on long flat surfaces.
Voids can be formed if gas cannot escape ahead of molten
metal (short run). Either low permeability or too much gas
produced (volatiles/steam). May need vent passages.
Penetration if sand too coarse, fluidity too high.
Hot tears or cracks can occur in long freezing range alloys
especially if casting is restrained by mould/cores during cooling
(poor collapsibility) Add cellulose.
Sand Properties and Defects
Lecture 3
31
Hand ramming. For small
number of castings. Pneumatic
hand rammer as well.
Moulding Machines
Jolting - sand on pattern then
drop flask several times to pack
sand.
Squeezing - platen/piston
squeezes sand against pattern.
Non-uniform sand density.
Combined Jolt & Squeezing -
Uniform density.
Making Sand Moulds
Lecture 3
32
Automatic mold making (eg. Disamatic Process)
Vertically parted, flaskless moulding machine.
Block of sand is pressed with RHS of casting
pattern on the left side and LHS of pattern/casting
on the RHS. Stacked in a line to give multiple
moulds (refer back to H-process). Good for mass
production
Making Sand Moulds
Vertically parted
flaskless moulding.
Lecture 3
33
Sand Cast Parts-Examples
Lecture 3
34
Disadvantages of
green sand can be
reduced.
Improved surface and
casting by drying mould
before casting.
Bake mould (150C)
- expensive, time
consuming.
Skin-dried mould -
just dry area near to
cavity e.g. using gas
torch.

Sand Moulds
Dry sand moulds are durable
Long time required for drying and increased
cost of operation
Compromise is skin dried mould
Commonly used for large castings
Binders (linseed oil etc) added in the sand
face to improve the strength of the skin
Lecture 3
35
Sodium Silicate - CO
2
molding
Sand mixed with 3-4% liquid sodium silicate to add strength.
Soft and mouldable until exposed to flow of CO
2
gas
Has poor Collapsibility (difficult to remove by shakeout)
Heating (due to metal pour) makes it more stronger
Additives that burn during pour increases collapsibility
Can use this material close to cavity upto 1 thickness and
then back-filed with regular moulding sand
If CO
2
is introduced only sand close to mould is hardened
without affecting the mould
Sand Moulds
Lecture 3
36
No-Bake, Air-Set or Chemically-bonded sands.
Alternative to sodium silicate
Use organic resin binders that cure at room temperature.
Binders mixed with sand just before moulding and curing
begins immediately
Limited working time before curing operation to be fast
After some time (depending on binder) the sand cures and
pattern can be withdrawn. After some more time to cure,
metal can be poured
Offers high dimensional accuracy, good strength and high
resistance to mould related casting defects
Patterns can have thinner section with deeper draws
Easy to shakeout as they decompose after metal pour
Sand Moulds
Lecture 3
37
Becoming increasingly popular; Better surface finish and dimensional
accuracy, higher production rate and reduced labour costs. Possible to
mechanize for mass production.
Make shell of sand+binder on hot metal pattern, bake, strip and clamp.
Less fettling as resin binder burns out due to heat from molten metal
Shell Moulding
Lecture 3
38
Use of metal pattern and finer sand (with smooth resin) gives smoother
surface and high dimensional accuracy (0.08 - 0.13mm).
More consistent casting. Thin shell increases permeability but gas evolution
is less due to less moisture in sand
Metal pattern (including runner & gates) cost is high & cost of binder, BUT
only thin shell produced (5-10mm).
High productivity etc economical for many cases (small to medium)
Shell Moulding
Lecture 3
39
Shell Moulding
Lecture 3
40
Other Sand Moulding Processes
Processes proposed to overcome limitations of traditional methods
V-process or vacuum molding - Draping a thin sheet of heat-
softened plastic over a special vented plastic pattern
The sheet is then drawn tightly to the pattern surface by a vacuum
A vacuum flask is then placed over the pattern, filled with sand, a
sprue and pouring cup are formed, and a second sheet of plastic is
placed over the mold
Vacuum is used to compact
the sand
The pattern vacuum is
released, and the pattern is
withdrawn.
FIGURE 14-19 Schematic of the V-process or vacuum molding. A) A
vacuum is pulled on a pattern, drawing a plastic sheet tightly against it. B)
A vacuum flask is placed over the pattern, filled with sand, a second sheet
placed on top, and a mold vacuum is drawn. C) The pattern vacuum is
then broken and the pattern is withdrawn. The mold halves are then
assembled, and the molten metal is poured.
Lecture 3
41
Other Sand Moulding Processes
Repeat for other segment, and the two mold halves are assembled.
Metal is poured while maintaining vacuum. Plastic film vaporizes
instantaneously. Vacuum is still sufficient to hold the sand in shape
until metal cools.
When the vacuum is released, the sand reverts to a loose,
unbonded state, and falls away from the casting.
No moisture-related defects. No binder cost. Dry sand is reusable.
Better surface finish since there is no clay, water, or other binder to
impair permeability, finer sands can be used,
Excellent Shakeout characteristics, since the mold collapses when
the vacuum is released.
Unfortunately, the process is relatively slow because of the steps
required
http://www.mccannsales.com/book/vprocess.pdf#search=%22v-process%20moulding%22
Lecture 3
42
For making internal cavities or reentrant sections (undercuts)
Increase moulding cost but reduce machining cost, wastage, allow design
versatility
Cores and Core Making
This part cannot
be cast without
use of cores
14 -21 shows 4 methods of making the pulley
Machining out the hole, making as 2 piece pattern (also
called green sand cores)
Green sand cores have low strength and difficult to do
long or complex sections
Lecture 3
43
Dry-sand cores independent to mould cavity. Make sand block that fits inside
cavity (resting in core-prints). Cast around core. Remove core as crumbled
sand. 14-21 C & D
Dump core box approach -
Mould sand + binder in core-box, baked and removed. Joined with
hot melt glue and fettled if necessary.
Coated with heat resistant material and to get smooth surface
(graphite, silica etc)
Simple cores can be pressed or extruded.
Complex cores can be done in core making
machines similar to injection moulding
Cores and Core Making
Lecture 3
44
Cores are fragile and the core making process should provide the required
strength for the cores.
Hot-Box method - A liquid thermosetting binder is added to sand and blown
into hot (230C) core-box. Cures quickly (10-30s) & removed.
Cold-Box method - Binder + sand blown into core-box and gas (e.g. SO2)
passed through to cure resin without heat. (gases are toxic ).
Air-set and no-bake sands (cold curing binder) and shell process can also be
used to make cores.
The advantages of these approaches include curing in room
temperature and in shell moulding hollow cores can be formed
Cores and Core Making
Lecture 3
45
Cores require:
Sufficient strength before hardening for handling
Sufficient hardness and strength after hardening to withstand
handling and molten metal. (wires may be added) 100-500psi
Good permeability to gases. (charcoal centre or venting)
Collapsibility. After pouring, core must be weak enough to allow
shrinkage, and also be easily removed on knock-out. (increase
this by using straw centre)
Adequate refractoriness. Usually surrounded by hot metals.
Smooth surface.
Minimum gas generation during pour.
Cores and Core Making
Lecture 3
46
Cores located/supported by:
Core prints in cavity (from pattern)
Extra supports (Chaplets) can be added. Like
internal chills these will become part of casting
(possible cause of defects - to be avoided).
Large enough to prevent full melting, and small
enough for surface to melt and fuse
Cores and Core Making
Lecture 3
47
Cores and Core Making
A pulley with recess on sides has reentrant
angles and can be made by two
approaches:
14-25 use of 3 piece process. Adding
an additional parting line enables use of
withdrawable patterns
No cores (green sand cores) good for
small runs
14-26 use of cores. Use simple green
sand mould together with ring shaped
cores
Reduced moulding time good for
large runs
Lecture 3
48
Other Processes Multi use patterns
Talc (MgO
2
) is added to prevent cracking, lime controls expansion,
glass fibers add strength and sand is used as filler.
Mould material added with water and additives poured over pattern
and allowed to cure. Mould is then removed from metal pattern
(complex patterns can be rubber too for easy removal)
Advantage - Good surface finish. Limitation Low MP metals/alloys
Plaster Mould Process
also known as Plaster of
Paris is the mold matl
Mixed with additives
Lecture 3
49
Ceramic Mould Process similar to
plaster but can withstand higher temp so
good for casting high MP metals/alloys
Cope and drag moulds are formed using ceramic slurry as mould
Thin sections can be done and good surface finish possible
Mould material is expensive. Can use a thin layer of ceramic material
backed with sand for large castings to reduce cost.
Other Processes Multi use patterns
Lecture 3
50
FIGURE 14-28 Method of combining
ceramic mold casting and wax pattern
casting to produce the complex vanes of an
impeller. A wax pattern is added to a metal
pattern. After the metal pattern is withdrawn
(Left), the wax pattern is melted out, leaving
a cavity as shown (Center), to produce the
casting (Right).
Other Processes Multi use patterns
Expendable graphite moulds - for metals like titanium (reactive when
hot) graphite mixed binder is used around the pattern and cured at
1000C. The pattern is removed and after casting, mould is broken.
Rubber-mould casting - artificial elastomers are cast around pattern.
Stripped from pattern (semi-rigid) to form mould. Good for low melting
point materials and metals (<260C) and for small castings.
Lecture 3
51
1. Investment casting - Produce a master pattern. (metal, wood, plastic).
2. From master pattern, produce a master die. (low-MP metal, steel,
wood). If low-MP metal or rubber molds are used, the die can be cast
from the master pattern. Steel dies may be machined without step 1
3. Produce wax patterns. Injecting molten wax into the master die. Cores
can be made with soluble wax and removed before ceramic coating.
4. Assemble the wax patterns onto a common wax sprue to produce a
pattern cluster, or tree to get better re entrant angles.
5. Coat the cluster with a thin layer of investment material. (dipping into a
watery slurry of finely ground refractory).
Expendable Mould and Pattern
Lecture 3
52
6. Produce the final investment around the coated cluster. (cluster is re-
dipped, but wet ceramic is coated with a layer of sand - process
repeated until desired thickness reached, or the single-coated
cluster can be placed upside down in a flask and liquid investment
material poured around it)
Vibrate the flask to remove entrapped air and settle the
investment material around the cluster. (performed when the
investment material is poured around the cluster)
7. Allow the investment to harden.
8. Melt or dissolve the wax pattern to remove it from the mold. (place
molds upside down in an oven - wax melts and runs out, any residue
subsequently vaporizes.
Investment Casting
Lecture 3
53
9. Preheat the mold in preparation for pouring. Heating to 1000 to
2000F (550 to 1100C) complete removal of wax, cures the mold to
give added strength, and allows the molten metal to retain its heat
and flow more readily to all thin sections. It also gives better
dimensional control because the mold and the metal will shrink
together during cooling.
10. Pour the molten metal. Various methods, beyond simple pouring,
can be used to ensure complete filling of the mold, especially when
complex, thin sections are involved. Among these methods are the
use of positive air pressure, evacuation of the air from the mold, and
a centrifugal process.
11. Remove casting from mould
Investment Casting
Lecture 3
54
Investment Flask Casting
Lecture 3
55
Investment Shell Casting
Lecture 3
56
Investment Casting
Lecture 3
57
1. EPS casting - Produce a pattern made of expanded polystyrene. For
small quantities, pattern can be cut by heated wires. Runners and
risers can be added by glue.
2. If large quantities are required, a metal mould is used to do single
use pattern. Beads of PS injected into the mould cavity and heated
where the expanded PS bonds together to form a complex bond.
For more complex patterns can be made in multiple sections and
glued
3. After patterning and gating attached, mould is done by
Full Mould method green sand with chemical additives 14-32
Lost Foam Method dipping in water based ceramic and powder
14-33
Evaporative Pattern Casting
Lecture 3
58
4. Mould metal poured inside the cavity without removing the pattern.
During the pour the metal vaporizes and replaces the EPS pattern.
5. After cooling the sand is dumped and the casting is taken out for
finishing.
6. Can make complex castings of both ferrous or non-ferrous metal
economically. No draft is required as well.
Evaporative Pattern Casting
Lecture 3
59
FIGURE 14-33 Schematic of
the lost-foam casting process.
In this process, the polystyrene
pattern is dipped in a ceramic
slurry, and the coated pattern is
surrounded with loose,
unbonded sand.
Evaporative Pattern Casting
Lecture 3
60
Evaporative Pattern Casting
Lecture 3
61
Final operation in casting is to separate casting from mould.
Shakeout is designed to do
Separate the moulds and remove casting from mould
Remove sand from flask and cores from cast
Punch out or vibratory machines are available for this task
Blast cleaning is done to remove adhering sand from casting,
or remove oxide scale and parting line burs.
Final finishing operations include Grinding, Turning or any
forms of machining
Shakeout, Cleaning and Finishing
Lecture 3
62
Types of Pattern