C95300 Aluminum Bronze Composition

This document provides information on aluminum bronze alloy C95300, including its chemical composition, mechanical properties, physical properties, fabrication practices, and thermal properties. Aluminum bronze C95300 can be cast or machined into solids, tubes, or rectangles from 1/2 to 15 inches. It has a tensile strength of 70 ksi (483 MPa) and is commonly used for electrical connectors, fasteners, industrial parts, and marine equipment due its strength and corrosion resistance at high temperatures. The alloy can be joined through brazing, gas shielded arc welding, or coated metal arc welding.

Uploaded by

Romeo Dequito
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
448 views2 pages

C95300 Aluminum Bronze Composition

This document provides information on aluminum bronze alloy C95300, including its chemical composition, mechanical properties, physical properties, fabrication practices, and thermal properties. Aluminum bronze C95300 can be cast or machined into solids, tubes, or rectangles from 1/2 to 15 inches. It has a tensile strength of 70 ksi (483 MPa) and is commonly used for electrical connectors, fasteners, industrial parts, and marine equipment due its strength and corrosion resistance at high temperatures. The alloy can be joined through brazing, gas shielded arc welding, or coated metal arc welding.

Uploaded by

Romeo Dequito
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
  • Product Overview
  • Properties & Specifications

C95300

Cast

Product Description:

Aluminum Bronze

Solids:

" to 9" OD

Tubes:

118" to 9" OD

Rectangles:

Up to 15"

Standard Lengths: 144"


Shape/Form:

semi-finished, mill stock or near-net shapes, anode, bar stock, billet/bloom, squares, hex, plate, profile or
structural shape, flats/rectangular bar

Typical Uses
Electrical

connectors

Fasteners

stripped nuts

Industrial

welding jaws, pickling hooks, high-strength clamps, valve bodies, pickling baskets, bearing segment for the
steel industry, large hold down screws, pressure blocks for the steel industry, gears, cams, high-temperature
applications, mining machine parts

Marine

covers for marine hardware, marine equipment

Note: Also available in a heat-treated condition..

Similar or Equivalent Specification


CDA

ASTM

C95300

B505

ASARCON

SAE

AMS

68B
J461
J462

FEDERAL

MILITARY

OTHER

QQ-C-390, G7
QQ-B-671, CLASS 2

MIL-B-16033, CLASS 2

ALUMINUM BRONZE 9B

Chemical Composition
Alloy

Cu%

Fe%

Al%

86.00

0.80-
1.50

9.0011.00

C95300

Chemical Composition according to ASTM B505/B505M-14


Note: Cu + Sum of Named Elements, 99.0% min. Single values represent maximums.

P.O. Box 816 Mars, PA 16046 Phone (724) 538-4000 Toll Free (800) 626-7071 Fax (724) 538-3956

Machinability

C95300 continued

Alloy

Machinability Rating

Density (lb/cu in.)

C95300

55

0.272

Mechanical Properties
Tensile Strength min

Yield Strength, at .5%


extension under load min

Elongation in 2 in. or
50 mm min

Brinell Hardness

ksi

MPa

ksi

MPa

typical BHN

70

483

26

179

25

125 (3000 kg)

Remarks

Mechanical Properties according to ASTM B505/B505M-14

Physical Properties
Melting Point Liquidus
Melting Point Solidus
Density
Specific Gravity
Electrical Resistivity
Electrical Conductivity
Thermal Conductivity
Coefficient of Thermal Expansion
Specific Heat Capacity
Modulas of Elasticity in Tension
Magnetic Permeability*

US Customary

Metric

1913 F
1904 F
0.272 lb/in3 at 68 F
7.530
80.20 ohms-cmil/ft at 68 F
13% IACS at 68 F
36.30 Btu ft/(hr ft2 F) at 68 F
90 10-6 per F (68-572 F)
0.090 Btu/lb/F at 68 F
16000 ksi
1.070

1045 C
1040 C
7.53 gm/cm3 at 20 C
7.53
13.33 microhm-cm at 20 C
0.075 MegaSiemens/cm at 20 C
62.8 W/m at 20 C
16.2 10-6 per C (20-300 C)
377.1 J/kg at 293 C
110000 MPa
1.07

Physical Properties provided by CDA


*Field Strength 8 kA/m

Fabrication Practices

Thermal Properties

Joining Technique

Suitability

Treatment

Temp./Time - US

Temp./Time - SI

Soldering
Brazing
Oxyacetylene Welding
Gas Shielded Arc Welding
Coated Metal Arc Welding

Good
Good
Not Recommended
Excellent
Good

Stress Temperature
Solution Minimum
Solution Maximum
Solution Time
Solution Medium
Precipitation Value
Precipitation Time
Precipitation Medium
Annealing Minimum
Annealing Maximum
Annealing Time
Hot Works Minimum
Hot Works Maximum

600
1585
1635
1.0
Water

316
863
891

1150
1225
1.0

622
663

Fabrication Properties provided by CDA

Thermal Properties provided by CDA